MORPHOLOGIES AND PERFORMANCE OF ORGANIC SOLAR CELLS USING LOW POLYMERIZATION DEGREE ALTERNATING COPOLYMER | |
Li GF ; Zuo Y ; Chen L ; Zhang JD ; Yan DH ; Qin DS | |
刊名 | acta polymerica sinica |
2013 | |
期号 | 2页码:183-190 |
关键词 | ENERGY-CONVERSION EFFICIENCY LOW-BANDGAP POLYMER CONJUGATED POLYMER DESIGN RULES ADDITIVES BLENDS DONORS FILMS |
ISSN号 | 1000-3304 |
通讯作者 | li gf |
中文摘要 | the ternary blend films composed of low polymerization degree poly[2,6-(4,4-bis-(2-ethylhexyl) - 4h-cyclopenta[2,1-b; 3,4-b']dithiophene)-alt-4,7-(2,1,3-benzothiadiazole)] (ldp-pcpdtbt), [6, 6]-phenyl-c61-butyric acid methyl ester (pc61bm), and polymethylmethacrylate (pmma) were fabricated with and without using 1, 8-dibromooctane (dbo) as solvent additive. the role of pmma was to enable the formation of the smooth and continuous thin films spun from the solution onto the conducting substrate. in addition, the good stability of the pmma against the heat, oxygen and water attacks was useful for achieving the long lifetime of organic solar cells. the ldp-pcpdtbt and pc bm phases in the pmma matrix were amorphous and crystalline, respectively, regardless of the additive processing. the crystalline aggregation of the ldp-pcpdtbt was hampered by the pc bm molecules, though the additive processing was able to promote the degree of crystallinity of the ldp-pcpdtbt. however, with the additive processing the phase separation of the ldp-pcpdtbt and pc bm components in the pmma matrix was optimized, leading to the improved electron-transporting property and thereby an increase of 32.4% in the power conversion efficiency of solar cell, compared to without the additive processing. the current research indicates that the low polymerization degree alternating copolymers can be recycled as efficient electron donors in association with pmma, helpful for reducing the material cost of organic solar cells. |
收录类别 | SCI收录期刊论文 |
语种 | 中文 |
WOS记录号 | WOS:000318196800006 |
公开日期 | 2014-04-16 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/50023] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Li GF,Zuo Y,Chen L,et al. MORPHOLOGIES AND PERFORMANCE OF ORGANIC SOLAR CELLS USING LOW POLYMERIZATION DEGREE ALTERNATING COPOLYMER[J]. acta polymerica sinica,2013(2):183-190. |
APA | Li GF,Zuo Y,Chen L,Zhang JD,Yan DH,&Qin DS.(2013).MORPHOLOGIES AND PERFORMANCE OF ORGANIC SOLAR CELLS USING LOW POLYMERIZATION DEGREE ALTERNATING COPOLYMER.acta polymerica sinica(2),183-190. |
MLA | Li GF,et al."MORPHOLOGIES AND PERFORMANCE OF ORGANIC SOLAR CELLS USING LOW POLYMERIZATION DEGREE ALTERNATING COPOLYMER".acta polymerica sinica .2(2013):183-190. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论