中文摘要 | Ion beam-assisted deposition (IBAD) technique has been used to deposit chromium nitride on the stainless steel substrates. Characterization and performance of this coating was carried out by a round-robin test at various laboratories. About 300 samples, prepared at Spire, USA, were distributed to 10 different laboratories. Characterization of coated materials, carried out using Rutherford backscattering (RBS), X-ray diffraction(XRD), glancing X-ray diffraction, Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS), confirmed a well-adherent layer of chromium nitride with composition and thickness of Cr0.8N0.2 and 1.2 mu m, respectively. The performance of the coating was tested by tribological tests: dynamic micro-indentation, micro-hardness, wear and friction, and corrosion tests. The coating was found to be hard with good wear resistance and had enhanced resistance to corrosion in acid media. (C) 2000 Elsevier Science B.V. All rights reserved. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-24 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/50972] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Guo, Z,Li, Y,Yan, J,et al. Photophysical properties of a crown ether-bearing [60]fulleropyrrolidine[J]. APPLIED PHYSICS B-LASERS AND OPTICS,2000,70(2):257. |
APA | Guo, Z.,Li, Y.,Yan, J.,Bai, F.,Li, F.,...&Ye, P.(2000).Photophysical properties of a crown ether-bearing [60]fulleropyrrolidine.APPLIED PHYSICS B-LASERS AND OPTICS,70(2),257. |
MLA | Guo, Z,et al."Photophysical properties of a crown ether-bearing [60]fulleropyrrolidine".APPLIED PHYSICS B-LASERS AND OPTICS 70.2(2000):257. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论