Diffusion of implanted Mo in Zr57Nb5Cu15.4Ni12.6Al10 non-crystalline alloy | |
Wang, XY ; Gao, M ; Sun, LL ; Liu, RP ; Zhang, J ; Wang, WK | |
刊名 | ACTA PHYSICA SINICA |
2004 | |
卷号 | 53期号:1页码:200 |
关键词 | SUPERCOOLED LIQUID REGION NI AMORPHOUS-ALLOYS METALLIC-GLASS DECOMPOSITION CRYSTALLIZATION TEMPERATURE DEPENDENCE MELTS |
ISSN号 | 1000-3290 |
通讯作者 | Wang, XY: Yanshan Univ, Coll Mat Sci & Engn, Key Lab Metastable Mat Sci & Technol, Qinhuangdao 066004, Peoples R China. |
中文摘要 | The effect of Co substitution and stabilizing elements on the structure and magnetic properties of Nd3Fe29-x-yCoxMy (M = Ti, V, Cr) compounds was investigated by means of x-ray diffraction and magnetic measurements. The results show that all the synthesized compounds have been. crystallized in Nd-3 ( Fe, Ti)(29) type structure with monoclinic symmetry and space group A2/m The solution of Co element in the compounds is different for the different stabilizing elements. For Cr as the stabilizing element, the pure Co-based 3 :29 phase could be obtained and the higher Cr content is required to stabilize the phase with increasing Co content. For Ti and V, the solution of Co in the compounds could be only 6.63 and 12 atoms, respectively. All the Nd-3 ( Fe, Co, M)(29) compounds show easy-planar type anisotropy at room temperature. For the Nd-3( Fe, Co, V)(29) compounds, the Curie temperature and saturation magnetization increase first and then decrease with further increasing Co content. The spin reorientation temperature shows and increasing tendency except the minimum for x = 6 due to the preferential occupation of Co atoms. For the Nd-3 (Fe, Co, Cr)(29) compounds, the Curie temperature increases first and then decreases with increasing Co content, but the magnetization is difficult to be saturated and only shows a decreasing tendency. The spin reorientation transition was only observed for the samples with x = 0 and 6. |
收录类别 | SCI |
语种 | 中文 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/35961] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Wang, XY,Gao, M,Sun, LL,et al. Diffusion of implanted Mo in Zr57Nb5Cu15.4Ni12.6Al10 non-crystalline alloy[J]. ACTA PHYSICA SINICA,2004,53(1):200. |
APA | Wang, XY,Gao, M,Sun, LL,Liu, RP,Zhang, J,&Wang, WK.(2004).Diffusion of implanted Mo in Zr57Nb5Cu15.4Ni12.6Al10 non-crystalline alloy.ACTA PHYSICA SINICA,53(1),200. |
MLA | Wang, XY,et al."Diffusion of implanted Mo in Zr57Nb5Cu15.4Ni12.6Al10 non-crystalline alloy".ACTA PHYSICA SINICA 53.1(2004):200. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论