Effect of cobalt on the mechanical properties of 718 base alloy with 1.2 wt % Al | |
Yao, Xiaoyu1,2,3; Liu, Fang2; Liu, Jiaao2,3; Xin, Xin2; Qi, Feng2; Sun, Wenru2 | |
刊名 | JOURNAL OF ALLOYS AND COMPOUNDS |
2022-12-10 | |
卷号 | 926页码:11 |
关键词 | Alloy 718 Cobalt Laves ?' ?? Mechanical properties |
ISSN号 | 0925-8388 |
DOI | 10.1016/j.jallcom.2022.166817 |
通讯作者 | Yao, Xiaoyu(xyyao15s@imr.ac.cn) |
英文摘要 | In this paper, the effect of Co (0-5 wt%) on the mechanical properties of 718 alloy and its strengthening mechanism were studied to clarify the function of Co on the mechanical properties of 718 base alloy. The experimental results showed that the addition of Co refined the grain. After the heat treatment, the addition of Co promoted the precipitation of Laves phase and gamma ' phase, but inhibited the precipitation of gamma '' phase. With the increasing of the Co content, the tensile strength was increased first and then decreased. It was found that the increase in the tensile strength of the alloy was caused by refining the grains and promoting the intergranular precipitation of the Laves phase. Nevertheless, Co increased the volume fraction of intragranular gamma ' phase, while suppressed the precipitation of intragranular precipitation of gamma '', thus the intragranular strength of the alloy was reduced. Accordingly, the alloy with 3 wt% Co shows the highest yield strength among the experimental alloys. Besides, the Co content extent 3 wt% will show a yield plateau under room temperature tension, but not in the case of 650 degrees C tension. It was revealed by analyzing the TEM morphology of the Laves phase in the room-temperature tensile samples and 650 degrees C tensile samples that the dislocation could shear through the intergranular Laves phase under the 650 degrees C tensile test, but it was not the case under room temperature tensile test. Therefore, the yield plateau in the stress-strain curves is due to the intergranular Laves phase impeding the dislocation motion.(c) 2022 Elsevier B.V. All rights reserved. |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000848442300003 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/175046] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Yao, Xiaoyu |
作者单位 | 1.72 Wenhua Rd, Shenyang, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.Univ Sci & Technol China, Coll Mat Sci & Engn, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Yao, Xiaoyu,Liu, Fang,Liu, Jiaao,et al. Effect of cobalt on the mechanical properties of 718 base alloy with 1.2 wt % Al[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2022,926:11. |
APA | Yao, Xiaoyu,Liu, Fang,Liu, Jiaao,Xin, Xin,Qi, Feng,&Sun, Wenru.(2022).Effect of cobalt on the mechanical properties of 718 base alloy with 1.2 wt % Al.JOURNAL OF ALLOYS AND COMPOUNDS,926,11. |
MLA | Yao, Xiaoyu,et al."Effect of cobalt on the mechanical properties of 718 base alloy with 1.2 wt % Al".JOURNAL OF ALLOYS AND COMPOUNDS 926(2022):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论