Mechanical properties and microstructure of pure copper joints brazed with amorphous Cu68.5Ni15.7Sn9.3P6.5 filler metal | |
Zhang, Jing1; Yu, Weiyuan2; Lu, Wenjiang2 | |
刊名 | International Journal of Simulation: Systems, Science and Technology |
2016 | |
卷号 | 17期号:24 |
关键词 | Brittle fracture Buildings Filler metals Fillers Housing Joints (structural components) Microstructure Tensile strength Vacuum brazing Vacuum furnaces Amorphous fillers Bonding mechanism Brazing joints Brazing temperature Contact reaction Dwelling time Fractured surfaces Properties and microstructures |
ISSN号 | 14738031 |
DOI | 10.5013/IJSSST.a.17.24.19 |
英文摘要 | Pure Cu is brazed with amorphous Cu68.5Ni15.7Sn9.3P6.5 (wt.%) filler metal in a vacuum furnace. The effects of dwelling time and brazing temperature on the tensile strength and microstructure of the brazed joints are investigated. The bonding mechanism of the joints is also discussed. It is found that the tensile strength firstly increased and then decreased with increasing dwelling time or brazing temperature. The brazed joints contain -Cu13.7Sn86.7, -phase Cu3P and (CuNi)2P phase. The content of brittle Cu3P governs the tensile strength of the joints. The maximum tensile strength of the brazing joints is found to be 135 MPa when brazing was performed at 680°C for 20 min. In addition, the bonding mechanism of the joints shows the characteristics of contact reaction brazing before the temperature reaches the melting point. The fractured surface is characterized by brittle fracture. © 2016, UK Simulation Society. All Rights Reserved. |
语种 | 英语 |
出版者 | UK Simulation Society, Clifton Lane, Nottingham, NG11 8NS, United Kingdom |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/113032] |
专题 | 实验室建设与管理处 |
作者单位 | 1.School of Physics and Mechanical-Electrical Engineering, Hexi University, Zhangye; Gansu; 734000, China; 2.State Key Laboratory for Non-ferrous Metal New Materials, Lanzhou University of Technology, Lanzhou; Gansu; 730050, China |
推荐引用方式 GB/T 7714 | Zhang, Jing,Yu, Weiyuan,Lu, Wenjiang. Mechanical properties and microstructure of pure copper joints brazed with amorphous Cu68.5Ni15.7Sn9.3P6.5 filler metal[J]. International Journal of Simulation: Systems, Science and Technology,2016,17(24). |
APA | Zhang, Jing,Yu, Weiyuan,&Lu, Wenjiang.(2016).Mechanical properties and microstructure of pure copper joints brazed with amorphous Cu68.5Ni15.7Sn9.3P6.5 filler metal.International Journal of Simulation: Systems, Science and Technology,17(24). |
MLA | Zhang, Jing,et al."Mechanical properties and microstructure of pure copper joints brazed with amorphous Cu68.5Ni15.7Sn9.3P6.5 filler metal".International Journal of Simulation: Systems, Science and Technology 17.24(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论