Thermodynamic Analysis and Experimental Investigation of Mg-9Zn-XAl Alloy for Semi-Solid Forming | |
Li Chun2; Cui Le3; Fan Xinhui2; Chen Jian2; Li Ying3; Yuan Xunfeng3; Li Yuandong1 | |
刊名 | 稀有金属材料与工程
![]() |
2019 | |
卷号 | 48期号:6页码:1769-1776 |
关键词 | thermodynamic calculation Mg-9Zn-XAl semi-solid forming phase transformation |
ISSN号 | 1002-185X |
英文摘要 | Solidification temperature range, temperature sensitivity of the solid fraction, temperature process window and phase composition and transformation path of Mg-9Zn-XAl (X=2, 4, 6, wt%) alloys were calculated by Pandat calculation, and studied by experiment. The results indicate that a larger temperature window is conducive to the control and operation of semi-solid forming for the Mg-9Zn-XAl alloy. The temperature sensitivity of all solid fractions is smaller than 0.015. Mg-9Zn-XAl alloys have different transformation temperatures and paths of the phase at different Al additions. alpha-Mg, MgZn, Mg32(Al, Zn)49 and Al5Mg11Zn4 are formed in all samples. When Al addition is increased to 6%, Mg17Al12 phase is formed. The grain size and roundness of Mg-9Zn-XAl alloys prepared by self-inoculation rheo-diecasting method are 65.3, 56.5, 52.2 mum and 1.3, 1.19, 1.23, respectively. When the working temperature is 150 °C, the comprehensive strength and deformation are 278, 283, 295 MPa and 36.22%, 33.02%, 31.21%, respectively. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
CSCD记录号 | CSCD:6517616 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/75004] ![]() |
专题 | 发展规划处 |
作者单位 | 1.Lanzhou University of Technology, State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou, Gansu 730050, China 2.Shangluo University;;Xian Technological University, Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources;;, Shangluo;;Xian, ;; 726000;;710021 3.Shangluo University, Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources, Shangluo, Shaanxi 726000, China |
推荐引用方式 GB/T 7714 | Li Chun,Cui Le,Fan Xinhui,et al. Thermodynamic Analysis and Experimental Investigation of Mg-9Zn-XAl Alloy for Semi-Solid Forming[J]. 稀有金属材料与工程,2019,48(6):1769-1776. |
APA | Li Chun.,Cui Le.,Fan Xinhui.,Chen Jian.,Li Ying.,...&Li Yuandong.(2019).Thermodynamic Analysis and Experimental Investigation of Mg-9Zn-XAl Alloy for Semi-Solid Forming.稀有金属材料与工程,48(6),1769-1776. |
MLA | Li Chun,et al."Thermodynamic Analysis and Experimental Investigation of Mg-9Zn-XAl Alloy for Semi-Solid Forming".稀有金属材料与工程 48.6(2019):1769-1776. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论