Study on Corrosion Deterioration of Reinforced Concrete Under Constant Acceleration Test Based on Double Stress | |
Shang, Minggang1; Zhang, Yunsheng1; He, Zhongmao1,2; Qiao, Hongxia1; Feng, Qiong1; Xue, Cuizhen1; Han, Zhao1 | |
刊名 | Cailiao Daobao/Materials Reports |
2022-06-10 | |
卷号 | 36期号:11 |
关键词 | Chlorine compounds Corrosive effects Deterioration Durability Electrochemical corrosion Electrochemical impedance spectroscopy Ions Maximum likelihood estimation Paraffins Acceleration tests Chloride ions Constant acceleration Constant current acceleration Constant-current Corrosion influence factor Current acceleration Log-normal distribution Maximum-likelihood estimation Paraffin isolation layer |
ISSN号 | 1005-023X |
DOI | 10.11896/cldb.21030289 |
英文摘要 | In view of the characteristics of long durability test period and large data dispersion of reinforced concrete, high corrosive saline soil was selec-ted as conductive medium to design constant accelerated corrosion test. In this work, the deterioration process of the one-dimensional and the three-dimensional reinforced concrete specimens under double stress of constant current and corrosive ions was simulated. Electrochemical impedance spectroscopy (AC impedance) data, chloride ion content data, and microscopic and macroscopic morphology data were collected during the accelerated test. Meanwhile, a statistical model of corrosion degradation in constant acceleration test based on lognormal distribution was established. The results have shown that the paraffin protective layer can increase the average life of reinforced concrete under chloride stress, constant current stress, and double stress by 249 h, 268 h and 115 h, respectively.The constant current stress firstly acts on the reinforced concrete, and the appearance of penetrating crack accelerates the corrosion effect of chloride ion stress. Finally, the double stress superposition increases the corrosion deterioration rate of reinforced concrete. The deterioration model of constant addition test based on lognormal distribution can realize the quantitative analysis of the protective effect of paraffin, and the influence factors of paraffin under chloride ion, constant current and double stress are 0.41, 0.35 and 0.19, respectively. © 2022, Materials Review Magazine. All right reserved. |
语种 | 中文 |
出版者 | Cailiao Daobaoshe/ Materials Review |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/159068] |
专题 | 土木工程学院 |
作者单位 | 1.School of Civil Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.College of Science & Technology Ningbo University, Ningbo; 315211, China |
推荐引用方式 GB/T 7714 | Shang, Minggang,Zhang, Yunsheng,He, Zhongmao,et al. Study on Corrosion Deterioration of Reinforced Concrete Under Constant Acceleration Test Based on Double Stress[J]. Cailiao Daobao/Materials Reports,2022,36(11). |
APA | Shang, Minggang.,Zhang, Yunsheng.,He, Zhongmao.,Qiao, Hongxia.,Feng, Qiong.,...&Han, Zhao.(2022).Study on Corrosion Deterioration of Reinforced Concrete Under Constant Acceleration Test Based on Double Stress.Cailiao Daobao/Materials Reports,36(11). |
MLA | Shang, Minggang,et al."Study on Corrosion Deterioration of Reinforced Concrete Under Constant Acceleration Test Based on Double Stress".Cailiao Daobao/Materials Reports 36.11(2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论