Fracture Behavior Analysis of Magnesium Oxychloride Cement Reinforced Concrete under Electric Corrosion | |
Chen, Kefan1; Qiao, Hongxia1,2; Wang, Penghui1; Peng, Kuan1; Zhu, Xiangchen1 | |
刊名 | Jianzhu Cailiao Xuebao/Journal of Building Materials |
2020-06-01 | |
卷号 | 23期号:3页码:557-562 |
关键词 | Cements Concrete construction Corrosion Crack propagation Crack tips Magnesium compounds Plates (structural components) Stress intensity factors Concrete cracking Electric corrosions Fracture behavior Fracture criteria Interfacial cracks Magnesium oxychloride cement Weight function method Weight functions |
ISSN号 | 10079629 |
DOI | 10.3969/j.issn.1007-9629.2020.03.011 |
英文摘要 | In order to obtain the critical rust expansion force of magnesium oxychloride cement reinforced concrete during cracking, the fracture behavior of magnesium oxychloride cement reinforced concrete under electric corrosion was studied based on fracture mechanics. According to Glinka-Shen weight function method, the weight function of square plate with single crack at hole edge was obtained by using the known stress intensity factor at crack tip under reference load. Then the formula of stress intensity factor at crack tip of square plate with single crack at hole edge was deduced. Finally, according to the fracture criterion of concrete, the formulas for calculating the critical rust expansion force of concrete cracking under electric corrosion and its variation law were given. The results show that with the increase of interfacial crack length, the stress intensity factor at crack tip increases while the critical rust expansion force decreases. The stress intensity factor at crack tip decreases with the increase of the diameter of reinforcing bar. © 2020, Editorial Department of Journal of Building Materials. All right reserved. |
语种 | 中文 |
出版者 | Tongji University |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/115395] |
专题 | 土木工程学院 |
作者单位 | 1.School of Civil Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Key laboratory of Disaster Prevention and Mitigation in Civil Engineering of Gansu Province, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Chen, Kefan,Qiao, Hongxia,Wang, Penghui,et al. Fracture Behavior Analysis of Magnesium Oxychloride Cement Reinforced Concrete under Electric Corrosion[J]. Jianzhu Cailiao Xuebao/Journal of Building Materials,2020,23(3):557-562. |
APA | Chen, Kefan,Qiao, Hongxia,Wang, Penghui,Peng, Kuan,&Zhu, Xiangchen.(2020).Fracture Behavior Analysis of Magnesium Oxychloride Cement Reinforced Concrete under Electric Corrosion.Jianzhu Cailiao Xuebao/Journal of Building Materials,23(3),557-562. |
MLA | Chen, Kefan,et al."Fracture Behavior Analysis of Magnesium Oxychloride Cement Reinforced Concrete under Electric Corrosion".Jianzhu Cailiao Xuebao/Journal of Building Materials 23.3(2020):557-562. |