Degradation Resistance and Reliability Analysis of Recycled Aggregate Concrete in a Sulfate Environment | |
Cao, Hui2; Zhao, Lifeng1; Lu, Chenggong2; Guan, Lijuan2; Qiao, Hongxia2; Li, Qiong2 | |
刊名 | ADVANCES IN MATERIALS SCIENCE AND ENGINEERING |
2020-03-16 | |
卷号 | 2020 |
ISSN号 | 1687-8434 |
DOI | 10.1155/2020/5217215 |
英文摘要 | Resistance to sulfate degradation is an important index used to measure concrete's durability. In this study, recycled aggregate concrete (RAC) with a 0%, 30%, and 50% recycled coarse aggregate substitution rate and a 0% and 15% recycled fine aggregate replacement rate was used as the research object, and its degradation resistance was evaluated by the mass loss rate and the relative dynamic modulus of elasticity. The degradation products were studied and analyzed with SEM scanning electron microscopy and XRD phase analysis. The relative dynamic modulus of elasticity was selected as the degradation index, the RAC concrete's degradation resistance was modeled by Wiener, and the reliability curve was obtained. The results showed that expansion products, such as gypsum and Ettringite, were produced in RAC concrete in a dry-wet sulfate cycling environment, and such defects as pores and voids were filled in the initial stage. The stress the expansion products exerted in the later stage caused the concrete to crack and peel, which demonstrated that the fluctuation law of mass and the dynamic elastic modulus increased first and then decreased. The recycled coarse aggregate substitution ratio's effect on RAC concrete is higher than that of recycled fine aggregate. The reliability curve established by the Wiener model can reflect the reliability of RAC concrete under different cycles well and can obtain RAC concrete's sulfate degradation resistance life with different aggregate substitution rates. |
资助项目 | National Natural Science Foundation of China[51868044][51468039] ; Gansu Natural Science Fund Project[2017GS10844] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | HINDAWI LTD |
WOS记录号 | WOS:000522979800004 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/64303] |
专题 | 土木工程学院 |
通讯作者 | Cao, Hui; Zhao, Lifeng |
作者单位 | 1.Lanzhou Univ Technol, Sch Design Art, Lanzhou, Gansu, Peoples R China 2.Lanzhou Univ Technol, Sch Civil Engn, Lanzhou, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Cao, Hui,Zhao, Lifeng,Lu, Chenggong,et al. Degradation Resistance and Reliability Analysis of Recycled Aggregate Concrete in a Sulfate Environment[J]. ADVANCES IN MATERIALS SCIENCE AND ENGINEERING,2020,2020. |
APA | Cao, Hui,Zhao, Lifeng,Lu, Chenggong,Guan, Lijuan,Qiao, Hongxia,&Li, Qiong.(2020).Degradation Resistance and Reliability Analysis of Recycled Aggregate Concrete in a Sulfate Environment.ADVANCES IN MATERIALS SCIENCE AND ENGINEERING,2020. |
MLA | Cao, Hui,et al."Degradation Resistance and Reliability Analysis of Recycled Aggregate Concrete in a Sulfate Environment".ADVANCES IN MATERIALS SCIENCE AND ENGINEERING 2020(2020). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论