Interface effects on he ion irradiation in nanostructured materials | |
Yang, Wenfan4,5; Pang, Jingyu4,5; Zheng, Shijian3,5,6; Wang, Jian1; Zhang, Xinghang7; Ma, Xiuliang2,5 | |
刊名 | Materials |
2019-08-01 | |
卷号 | 12期号:16 |
关键词 | Deterioration Ion bombardment Ions Nanostructured materials Radiation damage Swelling Cavities Energetic particles Ion irradiation damages Radiation induced defects Radiation-induced embrittlement Reactor materials Service lifetime Surface deterioration |
DOI | 10.3390/ma12162639 |
英文摘要 | In advanced fission and fusion reactors, structural materials suffer fromhigh dose irradiation by energetic particles and are subject to severe microstructure damage. He atoms, as a byproduct of the (n, α) transmutation reaction, could accumulate to form deleterious cavities, which accelerate radiation-induced embrittlement, swelling and surface deterioration, ultimately degrade the service lifetime of reactor materials. Extensive studies have been performed to explore the strategies that can mitigate He ion irradiation damage. Recently, nanostructured materials have received broad attention because they contain abundant interfaces that are efficient sinks for radiation-induced defects. In this review, we summarize and analyze the current understandings on interface effects on He ion irradiation in nanostructured materials. Some key challenges and research directions are highlighted for studying the interface effects on radiation damage in nanostructured materials. © 2019 by the authors. |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering ; Physics |
语种 | 英语 |
出版者 | MDPI AG, Postfach, Basel, CH-4005, Switzerland |
WOS记录号 | WOS:000484464800140 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114896] |
专题 | 材料科学与工程学院_特聘教授组 |
作者单位 | 1.Mechanical and Materials Engineering, University of Nebraska-Lincoln, Lincoln; NE; 68588, United States; 2.School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China 3.Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin; 300130, China; 4.School of Material Science and Engineering, University of Science and Technology of China, Hefei; 230026, China; 5.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang; 110016, China; 6.State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, Tianjin; 300130, China; 7.School of Materials Engineering, Purdue University, West Lafayette, Indiana; IN; 47907, United States; |
推荐引用方式 GB/T 7714 | Yang, Wenfan,Pang, Jingyu,Zheng, Shijian,et al. Interface effects on he ion irradiation in nanostructured materials[J]. Materials,2019,12(16). |
APA | Yang, Wenfan,Pang, Jingyu,Zheng, Shijian,Wang, Jian,Zhang, Xinghang,&Ma, Xiuliang.(2019).Interface effects on he ion irradiation in nanostructured materials.Materials,12(16). |
MLA | Yang, Wenfan,et al."Interface effects on he ion irradiation in nanostructured materials".Materials 12.16(2019). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论