The Influence of Multi-Phase Intermetallic Compounds on the Microstructure and Tribological Behaviors of 6061 Al Alloy by Adding AlCoCrFeNi High-Entropy Alloy | |
Li, Qinglin1; Bao, Xuepeng1; Fan, Chenglong1; Zhang, Xiaoyu2; Lan, Yefeng1 | |
刊名 | INTERNATIONAL JOURNAL OF METALCASTING |
2021-07 | |
卷号 | 16期号:2页码:871-877 |
关键词 | 6061 al alloy high-entropy alloy intermetallic compound aluminum matrix composites friction properties |
ISSN号 | 1939-5981 |
DOI | 10.1007/s40962-021-00631-6 |
英文摘要 | The AlCoCrFeNi high-entropy alloy (HEA) obtained by vacuum arc melting furnace was introduced into 6061 Al alloy, and a new aluminum matrix composites was prepared by traditional casting method. This paper mainly studies the changes in the microstructure and friction properties of the 6061 Al alloy after introducing 5.0 wt% HEA. With the help of testing apparatus such as optical microscope (OM), scanning electron microscope (SEM), electron probe microanalysis (EPMA), Vickers Hardness Tester and friction testing machine to analyze the microstructure and friction properties of AMCs. Results indicated that the addition of HEA lead to the precipitation of intermetallic compounds (AlCoFeNi, AlCrFe) and nano-scale AlCoFeNi phases with rod morphology distributing in the matrix alloy, and the average diameter of nanophases is approximately 200 nm. Compared with the 6061 Al alloy, the hardness and friction properties of the AMCs were significantly improved. The hardness of AMCs is extremely increased to 70 HV (6061Al alloy: 45.5HV). The coefficient of friction (COF) decreased by 61.8% from 1.78 to 0.68 and wear rate decreased by 43.4% from 2.56 x 10(-13) m(3)N(-1)m(-1) to 1.45 x 10(-13) m(3)N(-1)m(-1), when the introduction of HEA reached 5.0 wt%. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SPRINGER INTERNATIONAL PUBLISHING AG |
WOS记录号 | WOS:000669406400001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148866] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, Sch Mat Sci & Engn, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 2.Chongqing Univ Arts & Sci, Chongqing Engn Res Ctr New Energy Storage Devices, Chongqing 402160, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Qinglin,Bao, Xuepeng,Fan, Chenglong,et al. The Influence of Multi-Phase Intermetallic Compounds on the Microstructure and Tribological Behaviors of 6061 Al Alloy by Adding AlCoCrFeNi High-Entropy Alloy[J]. INTERNATIONAL JOURNAL OF METALCASTING,2021,16(2):871-877. |
APA | Li, Qinglin,Bao, Xuepeng,Fan, Chenglong,Zhang, Xiaoyu,&Lan, Yefeng.(2021).The Influence of Multi-Phase Intermetallic Compounds on the Microstructure and Tribological Behaviors of 6061 Al Alloy by Adding AlCoCrFeNi High-Entropy Alloy.INTERNATIONAL JOURNAL OF METALCASTING,16(2),871-877. |
MLA | Li, Qinglin,et al."The Influence of Multi-Phase Intermetallic Compounds on the Microstructure and Tribological Behaviors of 6061 Al Alloy by Adding AlCoCrFeNi High-Entropy Alloy".INTERNATIONAL JOURNAL OF METALCASTING 16.2(2021):871-877. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论