Effect of Zr content on crack formation and mechanical properties of IN738LC processed by selective laser melting | |
Hu, Yong1,2; Yang, Xiao-kang1,2; Kang, Wen-jiang1,2; Ding, Yu-tian1,2; Xu, Jia-yu1,2; Zhang, Hui-ying1,2 | |
刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA |
2021-05 | |
卷号 | 31期号:5页码:1350-1362 |
关键词 | selective laser melting IN738LC alloy Zr content solidification crack process parameter optimization mechanical properties |
ISSN号 | 1003-6326 |
DOI | 10.1016/S1003-6326(21)65582-6 |
英文摘要 | Two batches of commercial IN738LC alloy powders with different Zr contents were printed under the same parameters. The influences of Zr content (0.024 wt.% and 0.12 wt.%, respectively) in powders on crack density, distribution, formation mechanism and mechanical properties of selective laser melting (SLM)-treated parts were systematically studied. It was found that the crack density (area ratio) increases from 0.15% to 0.87% in the XOY plane and from 0.21% to 1.81% in the XOZ plane along with the Zr content increase from 0.024 wt.% to 0.12 wt.% in the original powders. Solidification cracks are formed along the epitaxially grown < 001 >-oriented columnar grain boundaries in molten pool center. The ultimate tensile strength of Sample 1 (0.024 wt.% Zr) is 1113 MPa, and there are dimples in tensile fracture. With an increase in the Zr content to 0.12 wt.% (Sample 2), the ultimate tensile strength of Sample 2 decreases to 610 MPa, and there are numerous original cracks and exposed columnar grain boundaries in tensile fracture. The optimization of printing parameters of Sample 2 considerably increases the ultimate tensile strength by 55.2% to 947 MPa, and the plasticity is greatly improved. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER |
WOS记录号 | WOS:000660035300001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148594] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Hu, Yong,Yang, Xiao-kang,Kang, Wen-jiang,et al. Effect of Zr content on crack formation and mechanical properties of IN738LC processed by selective laser melting[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2021,31(5):1350-1362. |
APA | Hu, Yong,Yang, Xiao-kang,Kang, Wen-jiang,Ding, Yu-tian,Xu, Jia-yu,&Zhang, Hui-ying.(2021).Effect of Zr content on crack formation and mechanical properties of IN738LC processed by selective laser melting.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,31(5),1350-1362. |
MLA | Hu, Yong,et al."Effect of Zr content on crack formation and mechanical properties of IN738LC processed by selective laser melting".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 31.5(2021):1350-1362. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论