Direct ink writing of TiC-316L metal matrix composites with an epoxy resin-absolute ethanol system | |
Lin, Tao3; Jin, Liu-Ping3; Yuan, Jia-Yun3; Shao, Hui-Ping3; Yu, Fu-Cheng1; Li, Wen-Yuan3; He, Xin-Bo3; Deng, Xin2,4 | |
刊名 | RARE METALS |
2021-03 | |
卷号 | 40期号:3页码:590-599 |
关键词 | DIW MMCs Epoxy resin TiC 316L |
ISSN号 | 1001-0521 |
DOI | 10.1007/s12598-020-01611-1 |
英文摘要 | TiC-316L metal matrix composites were successfully printed with an epoxy resin-absolute ethanol system by direct ink writing (DIW) process in this study. Microstructure and fracture morphology of the samples were observed by a scanning electron microscope (SEM). Also, the relative density, hardness and transverse rupture strength (TRS) of the sintered samples were tested. The results show that the samples prepared with a new epoxy resin-absolute ethanol system by the DIW process have high solid content of printing slurry, good surface roughness, high relative density and high strength. The solid content of the slurry suitable for DIW was 60 vol%, and the internal diameter of the nozzle was set to 0.4 mm, the printing speed was set to 30 mm center dot s(-1), and the layer height was set to 0.36 mm. For the sample with 35 wt% TiC-316L, the relative density, hardness and TRS of the sintered sample can reach 99.3%, HRA 79.5 and 1438 MPa, respectively. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | NONFERROUS METALS SOC CHINA |
WOS记录号 | WOS:000581559200004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148512] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China; 2.Guangdong Univ Technol, Sch Elect Engn, Guangzhou 510006, Peoples R China 3.Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Beijing 100083, Peoples R China; 4.Chengye Mans, Jihua Lab, Foshan 528299, Peoples R China; |
推荐引用方式 GB/T 7714 | Lin, Tao,Jin, Liu-Ping,Yuan, Jia-Yun,et al. Direct ink writing of TiC-316L metal matrix composites with an epoxy resin-absolute ethanol system[J]. RARE METALS,2021,40(3):590-599. |
APA | Lin, Tao.,Jin, Liu-Ping.,Yuan, Jia-Yun.,Shao, Hui-Ping.,Yu, Fu-Cheng.,...&Deng, Xin.(2021).Direct ink writing of TiC-316L metal matrix composites with an epoxy resin-absolute ethanol system.RARE METALS,40(3),590-599. |
MLA | Lin, Tao,et al."Direct ink writing of TiC-316L metal matrix composites with an epoxy resin-absolute ethanol system".RARE METALS 40.3(2021):590-599. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论