Direct ink writing of TiC–316L metal matrix composites with an epoxy resin–absolute ethanol system | |
Lin, Tao2; Jin, Liu-Ping2; Yuan, Jia-Yun2; Shao, Hui-Ping2; Yu, Fu-Cheng1; Li, Wen-Yuan2; He, Xin-Bo2; Deng, Xin3,4 | |
刊名 | Rare Metals |
2021-03-01 | |
卷号 | 40期号:3页码:590-599 |
关键词 | Ethanol Hardness Metallic matrix composites Morphology Scanning electron microscopy Sintering Surface roughness Titanium carbide Absolute ethanol Fracture morphology High relative densities High solid content Internal diameters Relative density Sintered samples Transverse rupture strength |
ISSN号 | 1001-0521 |
DOI | 10.1007/s12598-020-01611-1 |
英文摘要 | TiC–316L metal matrix composites were successfully printed with an epoxy resin–absolute ethanol system by direct ink writing (DIW) process in this study. Microstructure and fracture morphology of the samples were observed by a scanning electron microscope (SEM). Also, the relative density, hardness and transverse rupture strength (TRS) of the sintered samples were tested. The results show that the samples prepared with a new epoxy resin–absolute ethanol system by the DIW process have high solid content of printing slurry, good surface roughness, high relative density and high strength. The solid content of the slurry suitable for DIW was 60 vol%, and the internal diameter of the nozzle was set to 0.4 mm, the printing speed was set to 30 mm·s−1, and the layer height was set to 0.36 mm. For the sample with 35 wt% TiC–316L, the relative density, hardness and TRS of the sintered sample can reach 99.3%, HRA 79.5 and 1438 MPa, respectively. © 2020, GRINM Bohan (Beijing) Publishing Co., Ltd. |
语种 | 英语 |
出版者 | University of Science and Technology Beijing |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/147699] |
专题 | 材料科学与工程学院 |
作者单位 | 1.School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing; 100083, China; 3.Jihua Laboratory, Chengye Mansion, Foshan; 528299, China; 4.School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou; 510006, China |
推荐引用方式 GB/T 7714 | Lin, Tao,Jin, Liu-Ping,Yuan, Jia-Yun,et al. Direct ink writing of TiC–316L metal matrix composites with an epoxy resin–absolute ethanol system[J]. Rare Metals,2021,40(3):590-599. |
APA | Lin, Tao.,Jin, Liu-Ping.,Yuan, Jia-Yun.,Shao, Hui-Ping.,Yu, Fu-Cheng.,...&Deng, Xin.(2021).Direct ink writing of TiC–316L metal matrix composites with an epoxy resin–absolute ethanol system.Rare Metals,40(3),590-599. |
MLA | Lin, Tao,et al."Direct ink writing of TiC–316L metal matrix composites with an epoxy resin–absolute ethanol system".Rare Metals 40.3(2021):590-599. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论