Effect of Annealing Temperature on Microstructure and Mechanical Property of Hot-rolled M390 | |
Wang, Tiejun2,3; Yang, Bo1; Liang, Chen2,3; Che, Hongyan2,3; Qin, Wei2,3; Cao, Rui1 | |
刊名 | Cailiao Daobao/Materials Reports |
2020-06-25 | |
卷号 | 34期号:12页码:12122-12126 |
关键词 | Annealing Carbides Chromium steel Hot rolling Microstructure Scanning electron microscopy Tensile strength Thermal expansion Vickers hardness Annealing temperatures Carbide size Effect of annealing Ferrite matrix High temperature Microstructure and mechanical properties Rolling temperature X ray diffractometers |
ISSN号 | 1005023X |
DOI | 10.11896/cldb.19110119 |
英文摘要 | Hot-rolled M390 high-carbon and high-chromium martensitic stainless steel was annealed at 650, 750 and 850. Therefore, the changes of microstructure and mechanical properties of M390 under different initial rolling temperatures and different annealing temperatures after hot rolling were studied by thermal expansion machine, Vickers hardness tester, X-ray diffractometer and scanning electron microscope (SEM). The results show that the strength of M390 deteriorates but the plasticity increases significantly with the increase of annealing temperature after hot rolling, while the carbide size becomes larger and the number of carbides decreases. After initial rolling at a high temperature of 1 200 and then annealing at a high temperature of 850, M390's ferrite matrix uniformly distributed with fine spherical carbide. At this time, the best comprehensive mechanical properties with tensile strength of 920 MPa and elongation of 0.83% are obtained, which was facilitates to the subsequent processing and heat treatment of the material. © 2020, Materials Review Magazine. All right reserved. |
语种 | 英语 |
出版者 | Cailiao Daobaoshe/ Materials Review |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/115649] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metal, Lanzhou University of Technology, Lanzhou; 730050, China 2.Advanced Technology & Materials Co., Ltd., China Iron & Steel Research Institute Group, Beijing; 100081, China; 3.Engineering and Technology Research Center of Hot Isostatic Pressing, Zhuozhou; 072750, China; |
推荐引用方式 GB/T 7714 | Wang, Tiejun,Yang, Bo,Liang, Chen,et al. Effect of Annealing Temperature on Microstructure and Mechanical Property of Hot-rolled M390[J]. Cailiao Daobao/Materials Reports,2020,34(12):12122-12126. |
APA | Wang, Tiejun,Yang, Bo,Liang, Chen,Che, Hongyan,Qin, Wei,&Cao, Rui.(2020).Effect of Annealing Temperature on Microstructure and Mechanical Property of Hot-rolled M390.Cailiao Daobao/Materials Reports,34(12),12122-12126. |
MLA | Wang, Tiejun,et al."Effect of Annealing Temperature on Microstructure and Mechanical Property of Hot-rolled M390".Cailiao Daobao/Materials Reports 34.12(2020):12122-12126. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论