Morphology-controlled synthesis of orthorhombic LuFeO3particles via a hydrothermal route | |
Zhou, M.1; Yang, H.1,2; Xian, T.1; Ma, J.Y.2; Zhang, H.M.1; Feng, W.J.1; Wei, Z.Q.1; Jiang, J.L.1 | |
刊名 | Journal of Alloys and Compounds |
2014-12-25 | |
卷号 | 617页码:855-862 |
关键词 | Aspect ratio Hydrothermal synthesis Morphology Particle size Particle size analysis Sodium hydroxide Experimental parameters Ferromagnetic behaviors Formation mechanism Large particle sizes LuFeO3particles Morphological tailoring Morphology-controlled Reaction temperature |
ISSN号 | 09258388 |
DOI | 10.1016/j.jallcom.2014.08.057 |
英文摘要 | LuFeO3particles were synthesized via a hydrothermal route, where the influence of various experimental parameters on the products was systematically investigated. XRD analysis reveals that single o-LuFeO3samples can be synthesized at reaction temperatures of 160-260 °C, reaction times of 24-60 h, NaOH concentrations of 0.625-6.25 M, and Lu3+/Fe3+ion concentrations of 0.025-0.075 M. SEM observation shows that LuFeO3particles prepared at relatively low temperatures (160-220°C) and low NaOH concentrations (0.625-3.75 M) exhibit bar-like shape, and the aspect ratio of the bars decreases with increasing the temperature and NaOH concentration. At relatively high temperatures (240-260°C) and high NaOH concentrations (5-6.25 M), the resulted LuFeO3particles are shaped like spheres, polyhedrons or cubes. The samples prepared at the temperature of 220 °C and the NaOH concentration of 2.5-3.75 M have a relatively large particle size. All the particles exhibit a layered structure, indicating that they are mainly constructed from irregular sheets. Compared to the reaction temperature and NaOH concentration, the reaction time and Lu3+/Fe3+concentration has a relatively small effect on the morphology and size of LuFeO3particles. The as-prepared LuFeO3samples have a similar bandgap energy of 2.14 eV and exhibit a week ferromagnetic behavior at room temperature. © 2014 Elsevier B.V. All rights reserved. |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Elsevier Ltd |
WOS记录号 | WOS:000344135800139 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/113035] |
专题 | 理学院 材料科学与工程学院 |
作者单位 | 1.School of Science, Lanzhou University of Technology, Lanzhou; 730050, China 2.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; |
推荐引用方式 GB/T 7714 | Zhou, M.,Yang, H.,Xian, T.,et al. Morphology-controlled synthesis of orthorhombic LuFeO3particles via a hydrothermal route[J]. Journal of Alloys and Compounds,2014,617:855-862. |
APA | Zhou, M..,Yang, H..,Xian, T..,Ma, J.Y..,Zhang, H.M..,...&Jiang, J.L..(2014).Morphology-controlled synthesis of orthorhombic LuFeO3particles via a hydrothermal route.Journal of Alloys and Compounds,617,855-862. |
MLA | Zhou, M.,et al."Morphology-controlled synthesis of orthorhombic LuFeO3particles via a hydrothermal route".Journal of Alloys and Compounds 617(2014):855-862. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论