Microstructure and Property of Inconel 738 Alloy by Selective Laser Melting Forming | |
Xu Jiayu; Ding Yutian; Hu Yong; Gao Yubi; Chen Jianjun; Yang Qian | |
刊名 | RARE METAL MATERIALS AND ENGINEERING |
2019-11 | |
卷号 | 48期号:11页码:3727-3734 |
关键词 | selective laser melting (SLM) Inconel 738 alloy laser volume energy density density microstructure and property |
ISSN号 | 1002-185X |
英文摘要 | Effect of volume energy density on the relative density, microstructure and microhardness of Inconel 738 alloy fabricated by selective laser melting (SLM) was investigated by SEM, EBSD and OM. The results show that volume energy density plays a decisive role in the SLM forming process. With the increase of the volume energy density, the relative density increases first and then decreases. The highest relative density (99.4%) can be achieved at 65.2 J/mm(3). During solidification, the microstructure of Inconel 738 alloy formed by 2.44x105 K/s SLM has obvious anisotropy in vertical direction and parallel direction. The microstructure parallel to the building direction is "chess board", the vertical to building direction is "fish scale", and overlap zone between adjacent layers and neighbor tracks is the refined cellar grains. The microstructure shows obvious texture. With the increase of the laser volume energy density, the texture in the <100> direction increases gradually. The hardness of the sample increases with the increase of the laser volume energy density. When the laser volume density is higher than 65.2 J/mm(3), the hardness (HV) value of Inconel 738 alloy is higher than that of precision casting specimen (4100 MPa). |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000500083600044 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/64218] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Ding Yutian |
作者单位 | Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Xu Jiayu,Ding Yutian,Hu Yong,et al. Microstructure and Property of Inconel 738 Alloy by Selective Laser Melting Forming[J]. RARE METAL MATERIALS AND ENGINEERING,2019,48(11):3727-3734. |
APA | Xu Jiayu,Ding Yutian,Hu Yong,Gao Yubi,Chen Jianjun,&Yang Qian.(2019).Microstructure and Property of Inconel 738 Alloy by Selective Laser Melting Forming.RARE METAL MATERIALS AND ENGINEERING,48(11),3727-3734. |
MLA | Xu Jiayu,et al."Microstructure and Property of Inconel 738 Alloy by Selective Laser Melting Forming".RARE METAL MATERIALS AND ENGINEERING 48.11(2019):3727-3734. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论