Cold metal transfer joining aluminum alloys-to-galvanized mild steel | |
Cao, R.1; Yu, Gang1,2; Chen, J. H.1; Wang, Pei-Chung | |
刊名 | JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
![]() |
2013-10 | |
卷号 | 213期号:10页码:1753-1763 |
关键词 | Cold metal transfer Al sheet Steel sheet Join Weld-brazed joints |
ISSN号 | 0924-0136 |
DOI | 10.1016/j.jmatprotec.2013.04.004 |
英文摘要 | The cold metal transfer (CMT) welding-brazing process provides a potential method to join dissimilar metals. In this research, various 1 mm thick aluminum alloys were joined to 1 mm thick mild steel (Q235) by the CMT welding technology. It was found that it is feasible to join aluminum alloys-to-galvanized mild steel using the cold metal transfer method. The optimum process variables for weldability of aluminum-galvanized steel of dimension 200 mm x 50 mm x 1 mm could be obtained with a wire of A14043, 100% argon shielding gas, a welding voltage range of 12-14 V, a deviation distance range of 2-3.5 mm, a welding speed range of 6-8 mm/s and a wire-feed speed range of 4-6 m/min. The joint strength depended primarily on the thickness of the intermetallics and softening of the Al heat-affected-zone. By properly controlling the heat input (100-200 J/mm), the degradation of the HAZ property and thickness of the intermetallic reaction layer can be minimized, and consequently produced a hybrid aluminum-to-steel joint which had comparable strength to that of CMT weld-brazed Al-to-Al joint. (c) 2013 Elsevier B.V. All rights reserved. |
资助项目 | National Nature Science Foundation of China[51265028] |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000321482700011 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/34618] ![]() |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 |
通讯作者 | Cao, R. |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Gansu Adv Nonferrous Met Mat, Lanzhou 730050, Peoples R China 2.Jiangxi Hongdu Aviat Ind Grp Corp Ltd, Nanchang 330024, Peoples R China |
推荐引用方式 GB/T 7714 | Cao, R.,Yu, Gang,Chen, J. H.,et al. Cold metal transfer joining aluminum alloys-to-galvanized mild steel[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,2013,213(10):1753-1763. |
APA | Cao, R.,Yu, Gang,Chen, J. H.,&Wang, Pei-Chung.(2013).Cold metal transfer joining aluminum alloys-to-galvanized mild steel.JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,213(10),1753-1763. |
MLA | Cao, R.,et al."Cold metal transfer joining aluminum alloys-to-galvanized mild steel".JOURNAL OF MATERIALS PROCESSING TECHNOLOGY 213.10(2013):1753-1763. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论