Effect of Annealing Temperature on the Microstructure and Tensile Properties of a Bimodal Nano/Micro Grained 1020 Carbon Steel Prepared by Aluminothermic Reaction Casting | |
La, Peiqing; Guo, Xin; Wang, Hongding; Shi, Ting; Zhen, Xiaojuan; Wei, Fuan; Lu, Xuefeng | |
刊名 | METALS AND MATERIALS INTERNATIONAL |
2016-03 | |
卷号 | 22期号:2页码:236-242 |
关键词 | aluminothermic reaction casting scanning electron microscopy (SEM) metals annealing mechanical properties |
ISSN号 | 1598-9623 |
DOI | 10.1007/s12540-016-5343-z |
英文摘要 | Bulk 1020 carbon steel was prepared by aluminothermic reaction casting. After casting, isothermal aging treatments at different temperatures are performed for different periods up to 8 h. Microstructure characterization was performed using many methods, including optical microscopy, X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It was found that the steel consisted of a nanocrystalline-ferrite matrix and a microcrystalline pearlite phase with a laminar structure. The average grain sizes of the ferrite were 23, 24, 28, and 37 nm for the cast steel and for samples annealed at 600, 800, and 1000 degrees C, respectively. As the annealing temperature increased, the volume fraction of the pearlite initially increased and then decreased, while the laminar spacing of pearlite increased from 240 to 900 nm. When annealed at 1000 degrees C, a spherical black micron pearlite particle was formed. The tensile and yield strength dramatically decreased, and the elongation varied slightly with the annealing temperature. A ductile phase was achieved by extending the holding time. |
资助项目 | National Natural Science Foundation of China[51164022][51561020] ; Gansu Provincial Science and Technology Support Program[1304GK-CA027] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | KOREAN INST METALS MATERIALS |
WOS记录号 | WOS:000371651300011 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33751] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | La, Peiqing |
作者单位 | Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | La, Peiqing,Guo, Xin,Wang, Hongding,et al. Effect of Annealing Temperature on the Microstructure and Tensile Properties of a Bimodal Nano/Micro Grained 1020 Carbon Steel Prepared by Aluminothermic Reaction Casting[J]. METALS AND MATERIALS INTERNATIONAL,2016,22(2):236-242. |
APA | La, Peiqing.,Guo, Xin.,Wang, Hongding.,Shi, Ting.,Zhen, Xiaojuan.,...&Lu, Xuefeng.(2016).Effect of Annealing Temperature on the Microstructure and Tensile Properties of a Bimodal Nano/Micro Grained 1020 Carbon Steel Prepared by Aluminothermic Reaction Casting.METALS AND MATERIALS INTERNATIONAL,22(2),236-242. |
MLA | La, Peiqing,et al."Effect of Annealing Temperature on the Microstructure and Tensile Properties of a Bimodal Nano/Micro Grained 1020 Carbon Steel Prepared by Aluminothermic Reaction Casting".METALS AND MATERIALS INTERNATIONAL 22.2(2016):236-242. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论