Effectzs of minor Y,Zr and Er addition on microstructm and properties of Al-5Cu-0.4Mn alloy | |
Zhang, Feng1; Guo, Ting-biao1,2; Li, Qi1; Wang, Chen1; Ding, Wan-wu1,2; Li, Qing-lin1,2 | |
刊名 | CHINA FOUNDRY |
2017-11 | |
卷号 | 14期号:6页码:461-468 |
关键词 | Al-Cu-Mn alloy T6 heat treatment microstructure mechanical properties |
ISSN号 | 1672-6421 |
DOI | 10.1007/s41230-017-6130-2 |
英文摘要 | The effect of different contents of Y, Zr and Er on microstructure and properties of Al-5Cu-0.4Mn alloy was investigated. T6 heat treatment, OM, SEM and EDS methods were applied to the alloy. The results showed that fluidity and elongation of alloy adding Y, Zr and Er were improved, while with the increase of addition amounts, 8 phase increased and grains were trended to grow up gradually. The Al-5Cu-0.4Mn alloy presented the maxed style of ductile and brittle fracture. After T6 heat treatment, the precipitation amounts of 6 phase decreased dramatically and tensile strength and hardness significantly increased. Especially when addition contents were among 0.1-0.3wt.%, tensile strength and hardness of heat-treated alloy increased greatly, almost doubled as that of the as-cast state. The tensile strength reached its maximum of 378.43 MPa when the addition amount was 0.3wt.%. With the further increase of addition amounts, the elongation deteriorated and the proportion of ductile fracture reduced due to the limited dispersion strengthening effect of 6 phase and Al8Cu4Er. It demonstrated that addition of 0.1-0.3wt.% Y, Zr and Er would generate positive effects and influences on Al-5Cu-0.4Mn alloy, which is significant for optimizing components and improving properties of Al-5Cu-0.4Mn alloy. |
资助项目 | Gansu Province Science and Technology Major Special Program Foundation of China[1302GKDA015] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | FOUNDRY JOURNAL AGENCY |
WOS记录号 | WOS:000419899000001 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33035] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Guo, Ting-biao |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China 2.Minist Educ, Key Lab Nonferrous Alloys & Proc, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Feng,Guo, Ting-biao,Li, Qi,et al. Effectzs of minor Y,Zr and Er addition on microstructm and properties of Al-5Cu-0.4Mn alloy[J]. CHINA FOUNDRY,2017,14(6):461-468. |
APA | Zhang, Feng,Guo, Ting-biao,Li, Qi,Wang, Chen,Ding, Wan-wu,&Li, Qing-lin.(2017).Effectzs of minor Y,Zr and Er addition on microstructm and properties of Al-5Cu-0.4Mn alloy.CHINA FOUNDRY,14(6),461-468. |
MLA | Zhang, Feng,et al."Effectzs of minor Y,Zr and Er addition on microstructm and properties of Al-5Cu-0.4Mn alloy".CHINA FOUNDRY 14.6(2017):461-468. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论