Formation of stable equiaxial nanograined Al via combined plastic deformation

doi:10.1016/j.scriptamat.2021.114054

CORC > 兰州理工大学 > 兰州理工大学

	Formation of stable equiaxial nanograined Al via combined plastic deformation
	Wang, B.1,2; Xu, W.1; Zhou, X.1; Li, X. Y.1,2; Qiao, J. S.2
刊名	SCRIPTA MATERIALIA
	2021-10
卷号	203
关键词	High pressure torsion Nanograined Al Grain boundary relaxation
ISSN号	1359-6462
DOI	10.1016/j.scriptamat.2021.114054
英文摘要	Refining grains in pure aluminum (Al) to nanometerscale is difficult due to its low melting point and high stacking fault energy. Here, with a combined plastic deformation process of cold rolling and cryogenic high pressure torsion, equiaxial-nanograined pure Al with an average grain size of 65 nm was fabricated. Grain orientation statistics and high resolution transmission electron microscope observations revealed that most of the grain boundaries are high angle grain boundaries, in which there are plenty of low Sigma boundaries, indicating the occurrence of grain boundary relaxation. The equiaxial nanograined Al exhibited high strength and superior thermal stability due to the grain boundary relaxation. (C) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
WOS研究方向	Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	PERGAMON-ELSEVIER SCIENCE LTD
WOS记录号	WOS:000681318400009
内容类型	期刊论文
源URL	[http://ir.lut.edu.cn/handle/2XXMBERH/148916]
专题	兰州理工大学
作者单位	1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, 287 Langongping Rd, Lanzhou 730050, Peoples R China;
推荐引用方式 GB/T 7714	Wang, B.,Xu, W.,Zhou, X.,et al. Formation of stable equiaxial nanograined Al via combined plastic deformation[J]. SCRIPTA MATERIALIA,2021,203.
APA	Wang, B.,Xu, W.,Zhou, X.,Li, X. Y.,&Qiao, J. S..(2021).Formation of stable equiaxial nanograined Al via combined plastic deformation.SCRIPTA MATERIALIA,203.
MLA	Wang, B.,et al."Formation of stable equiaxial nanograined Al via combined plastic deformation".SCRIPTA MATERIALIA 203(2021).