Study of the mechanical properties and microstructures of conical joints for aluminum/steel continuous drive friction welding | |
Zhang, Changqing1,2; Wang, Shuwen2; Luo, Dechun3; Shi, Wenchen2; Liu, Xiao2; Cui, Guosheng2; Chen, Boyang2; Xin, Zhou3; Rui, Zhiyuan3 | |
刊名 | JOURNAL OF MANUFACTURING PROCESSES |
2021-07 | |
卷号 | 67页码:241-252 |
关键词 | Continuous drive friction welding Aluminum steel dissimilar joint Microstructure homogeneity Mechanical property Conical joint design |
ISSN号 | 1526-6125 |
DOI | 10.1016/j.jmapro.2021.04.070 |
英文摘要 | Presetting the taper on a joint will change the thermodynamic cycle of the interface in the direction of the rotating friction radius and affect the structure and joint mechanical properties. In this research, five types of conical Q235 low carbon steel rods at 5 degrees, 10 degrees, 15 degrees, 20 degrees, and 25 degrees were paired with 1060 aluminum rods performed with continuous drive friction welding butt joint experiments. For these experiments, the temperatures of the interface center as well as 1/3R and 2/3R were collected during the welding process. After welding, the joints were subjected to tensile testing, fracture analysis, and microstructure analysis of the joint interface. The results showed that for the same process parameters, the increase in the tilt angle of the conical end face made the corona bonds of the friction interface of the joint move from the outside to the inside due to a decrease in the friction heat and an increase in the tangential stress, and the corona bonds became narrower. For certain technological conditions, a reasonable cone could improve the homogenization of the radial intermetallic compounds at the joint interface. The thickness of the intermetallic compound layer of the 15 degrees tilt angle joints had the smallest gradient along the radius. The average thickness was about 0.85 mu m and the average tensile strength reached a maximum of 77.5 MPa. This was 96 % of the base material of 1060 pure aluminum. |
WOS研究方向 | Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000658510500001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148686] |
专题 | 机电工程学院 兰州理工大学 材料科学与工程学院 马克思主义学院 |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Non Ferrous Me, Lanzhou 730050, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China; 3.Lanzhou Univ Technol, Sch Mech & Elect Engn, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Changqing,Wang, Shuwen,Luo, Dechun,et al. Study of the mechanical properties and microstructures of conical joints for aluminum/steel continuous drive friction welding[J]. JOURNAL OF MANUFACTURING PROCESSES,2021,67:241-252. |
APA | Zhang, Changqing.,Wang, Shuwen.,Luo, Dechun.,Shi, Wenchen.,Liu, Xiao.,...&Rui, Zhiyuan.(2021).Study of the mechanical properties and microstructures of conical joints for aluminum/steel continuous drive friction welding.JOURNAL OF MANUFACTURING PROCESSES,67,241-252. |
MLA | Zhang, Changqing,et al."Study of the mechanical properties and microstructures of conical joints for aluminum/steel continuous drive friction welding".JOURNAL OF MANUFACTURING PROCESSES 67(2021):241-252. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论