Investigation of the role of silicon in TiAlSiN coating deposited on TiAl alloys during long-term oxidation

doi:10.1016/j.corsci.2022.110394

CORC > 金属研究所 > 中国科学院金属研究所

	Investigation of the role of silicon in TiAlSiN coating deposited on TiAl alloys during long-term oxidation
	Zhang, Kai 4,5; Xin, Li 5; Ma, Tianyu 3,5; Chang, Hao 4,5; Lu, Yiliang 4,5; Feng, Changjie 2; Zhu, Shenglong 5; Wang, Fuhui 1
刊名	CORROSION SCIENCE
	2022-08-01
卷号	204 页码:14
关键词	Titanium Intermetallic TEM Oxidation High temperature corrosion
ISSN号	0010-938X
DOI	10.1016/j.corsci.2022.110394
通讯作者	Xin, Li(xli@imr.ac.cn)
英文摘要	One challenge for TiAl alloys to serve above 800 degrees C is insufficient oxidation resistance. In this article, long-term oxidation of TiAlSiN coated Ti-45Al-2Nb-2Mn, Ti-48Al-2Cr-2Nb and Ti-50Al were investigated at 900 degrees C. The results showed Al2O3 top layer in oxide scale which formed during earlier stage of oxidation kept protective during long-term oxidation. Presence of SiO2 layer at oxide/coating interface and segregations of SiO2 at grain boundaries were observed. Oxygen inner diffusion and titanium outer diffusion was inhibited and coating exhibited excellent oxidation resistance. Stable Ti5Si3 diffusion barrier layer formed at TiAlSiN/TiAl interface due to Si inward diffusion helped coating maintaining long-term stability.
资助项目	National Natural Science Foundation of China[51871229] ; Liaoning Revitalization Talents Program[XLYC 2002031] ; China and Innovation Project for Postgraduate of Institute of Metal Research, Chinese Academy of Sciences, China
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	PERGAMON-ELSEVIER SCIENCE LTD
WOS记录号	WOS:000808358200001
资助机构	National Natural Science Foundation of China ; Liaoning Revitalization Talents Program ; China and Innovation Project for Postgraduate of Institute of Metal Research, Chinese Academy of Sciences, China
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/174341]
专题	金属研究所_中国科学院金属研究所
通讯作者	Xin, Li
作者单位	1.Northeastern Univ, Shenyang Natl Lab Mat Sci, 3-11 Wenhua Rd, Shenyang 110819, Peoples R China 2.Shenyang Aerosp Univ, Sch Mat Sci & Engn, 37 Daoyi South Ave, Shenyang 110136, Peoples R China 3.Northeastern Univ, Sch Mat Sci & Engn, 3-11 Wenhua Rd, Shenyang 110819, Peoples R China 4.Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Peoples R China 5.Chinese Acad Sci, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Kai,Xin, Li,Ma, Tianyu,et al. Investigation of the role of silicon in TiAlSiN coating deposited on TiAl alloys during long-term oxidation[J]. CORROSION SCIENCE,2022,204:14.
APA	Zhang, Kai.,Xin, Li.,Ma, Tianyu.,Chang, Hao.,Lu, Yiliang.,...&Wang, Fuhui.(2022).Investigation of the role of silicon in TiAlSiN coating deposited on TiAl alloys during long-term oxidation.CORROSION SCIENCE,204,14.
MLA	Zhang, Kai,et al."Investigation of the role of silicon in TiAlSiN coating deposited on TiAl alloys during long-term oxidation".CORROSION SCIENCE 204(2022):14.