A low-temperature hydrothermal synthesis of submicron spherical BaF2

doi:10.1039/d1ra06084h

CORC > 青海盐湖研究所 > 中国科学院青海盐湖研究所 > 盐湖资源综合利用工程技术中心

	A low-temperature hydrothermal synthesis of submicron spherical BaF2
	Li, Xiao; Zhao, Yuxiang; Li, Bo; Wang, Shuxuan; Zou, Xingwu
刊名	RSC ADVANCES
	2021-12-16
卷号	11 期号:63 页码:40051-40058
DOI	10.1039/d1ra06084h
英文摘要	The sub-micron spherical barium fluoride (BaF2) was successfully synthesized via a low-temperature hydrothermal method using ethylenediamine tetraacetic acid disodium salt (EDTA-2Na) as the chelating agent. The effect of pH, the molar ratio of EDTA to Ba2+, barium hydroxide octahydrate (Ba(OH)(2)center dot 8H(2)O) concentration, hydrofluoric acid (HF) concentration, hydrothermal temperature and time, on the formation of spherical BaF2 were investigated. The formation mechanism of spherical BaF2 has been proposed based on the experimental results. The results show that the spherical BaF2, with an average size of 346.9 nm, is formed by the self-assembly of nanocubes. The optimized synthesis conditions are: pH = 14, EDTA-2Na : Ba2+ = 1 : 1, Ba(OH)(2) concentration is 0.1 mol L-1, HF concentration is 2.0 mol L-1, hydrothermal temperature is 80 degrees C and hydrothermal time is 2.0 h. The self-assembly mechanism of the spherical secondary structure was revealed from the perspective of crystal nucleation and growth, and the important role of EDTA in the spherical BaF2 formation is explained.
内容类型	期刊论文
源URL	[http://ir.isl.ac.cn/handle/363002/34193]
专题	青海盐湖研究所_盐湖资源综合利用工程技术中心
推荐引用方式 GB/T 7714	Li, Xiao,Zhao, Yuxiang,Li, Bo,et al. A low-temperature hydrothermal synthesis of submicron spherical BaF2[J]. RSC ADVANCES,2021,11(63):40051-40058.
APA	Li, Xiao,Zhao, Yuxiang,Li, Bo,Wang, Shuxuan,&Zou, Xingwu.(2021).A low-temperature hydrothermal synthesis of submicron spherical BaF2.RSC ADVANCES,11(63),40051-40058.
MLA	Li, Xiao,et al."A low-temperature hydrothermal synthesis of submicron spherical BaF2".RSC ADVANCES 11.63(2021):40051-40058.