THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE

doi:10.13168/cs.2019.0030

CORC > 青海盐湖研究所 > 中国科学院青海盐湖研究所 > 盐湖资源与化学实验室

	THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE
	Huang, Qing; Li, Ying; Chang, Chenggong; Zheng, Weixin; Wen, Jing; Dong, Jinmei; Man, Yangyang; Danchun, A.; Xiao, Xueying; Zhou, Yuan
刊名	CERAMICS-SILIKATY
	2019
卷号	63 期号:4 页码:347-355
ISSN号	0862-5468
DOI	10.13168/cs.2019.0030
英文摘要	In this paper, the performance of magnesium oxychloride cement (MOC) in brine environment after the addition of an anti-corrosion admixture (Q101) was investigated. The compressive strength, compressive strength retention, crystal composition and microstructure were analysed in detail. The results show that the compressive strength of the MOC with the Q101 admixture maintains a high compressive strength of more than 100 MPa in air, and decreases slightly in the raw brine and the aging brine, but the decreases are not significant with the compressive strength of 80 MPa. This demonstrates the excellent salt brine resistance in brine environment of the MOC. One reason is that the high content of Mg2+ and Cl- in brine suppress the dissolution rate of main hydration product in the MOC. The other is the addition of an anti-corrosion additive that improves the salt brine resistance by about 30 %. However, the compressive strength and strength retention of the MOC after the raw brine immersion are higher than the aging brine immersion. The reason may be that the salts fill the surface and the pores in the samples that prevented water erosion to some extent. Meanwhile, the MOC pastes have the biggest compressive strength retention when the Q101 was up to 10 % over the long run. As a result, the optimum dosage of Q101 is 10 % in this experiment.
内容类型	期刊论文
源URL	[http://ir.isl.ac.cn/handle/363002/34081]
专题	青海盐湖研究所_盐湖资源与化学实验室中国科学院青海盐湖研究所
推荐引用方式 GB/T 7714	Huang, Qing,Li, Ying,Chang, Chenggong,et al. THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE[J]. CERAMICS-SILIKATY,2019,63(4):347-355.
APA	Huang, Qing.,Li, Ying.,Chang, Chenggong.,Zheng, Weixin.,Wen, Jing.,...&Zhou, Yuan.(2019).THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE.CERAMICS-SILIKATY,63(4),347-355.
MLA	Huang, Qing,et al."THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE".CERAMICS-SILIKATY 63.4(2019):347-355.