Improving fatigue life of 7N01 Al alloy weld by surface spinning strengthening | |
Wang, Dongqiqiong1,3,4; Wang, Suhuan2; Wang, Qiang4; Hou, Jiapeng4; Li, Xiaowu1,3; Zhang, Zhefeng4 | |
刊名 | FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
![]() |
2021-05-21 | |
页码 | 13 |
关键词 | Al alloy fatigue fatigue life surface strengthening welded joint |
ISSN号 | 8756-758X |
DOI | 10.1111/ffe.13514 |
通讯作者 | Wang, Qiang(gmwang@imr.ac.cn) ; Li, Xiaowu(xwli@mail.neu.edu.cn) ; Zhang, Zhefeng(zhfzhang@imr.ac.cn) |
英文摘要 | The purpose of this study is to improve the surface microstructure and mechanical properties of 7N01 Al alloy welded joints by surface spinning strengthening (3S), so as to improve the fatigue life at certain stress. Results show that after the 3S treatment, the microhardness of the welded joint increases significantly due to the introduction of some nanoprecipitates and dislocations, and the strength and elongation increase simultaneously. The minimum fatigue life of the welded specimen under the condition of maximum stress of 150 MPa and stress ratio of 0.1 is increased from less than 10(6) cycles to more than 3 x 10(6) cycles after the 3S treatment. Fracture surface analysis shows that the crack initiation site of the sample with welded joint is turned from the surface to the subsurface after 3S treatment, which is beneficial to the elimination of surface defect and the improvement of surface strength. |
资助项目 | LiaoNing Revitalization Talents Program[XLYC1808027] ; National Natural Science Foundation of China[51871048] |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | WILEY |
WOS记录号 | WOS:000652755500001 |
资助机构 | LiaoNing Revitalization Talents Program ; National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/161086] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Wang, Qiang; Li, Xiaowu; Zhang, Zhefeng |
作者单位 | 1.Northeastern Univ, Minist Educ, Key Lab Anisotropy & Texture Mat, Wenhua Rd, Shenyang 110819, Peoples R China 2.CRRC Sifang Co Ltd, Engn Dept, Qingdao, Peoples R China 3.Northeastern Univ, Sch Mat Sci & Engn, Dept Mat Phys & Chem, Wenhua Rd, Shenyang 110819, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, 72 Wenhua Rd, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Dongqiqiong,Wang, Suhuan,Wang, Qiang,et al. Improving fatigue life of 7N01 Al alloy weld by surface spinning strengthening[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,2021:13. |
APA | Wang, Dongqiqiong,Wang, Suhuan,Wang, Qiang,Hou, Jiapeng,Li, Xiaowu,&Zhang, Zhefeng.(2021).Improving fatigue life of 7N01 Al alloy weld by surface spinning strengthening.FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,13. |
MLA | Wang, Dongqiqiong,et al."Improving fatigue life of 7N01 Al alloy weld by surface spinning strengthening".FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES (2021):13. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论