Improved oxidation resistance of gamma-TiAl intermetallics by sputtered Ni plus CrAlYHfSiN composite coating | |
Yang, Yingfei1; Xiao, Qin1; Ren, Pan1; Li, Wei1; Zhu, Shenglong2; Wang, Fuhui3 | |
刊名 | CORROSION SCIENCE |
2021-07-15 | |
卷号 | 187页码:11 |
关键词 | High temperature coating Oxidation MCrAlY Thermal stress |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2021.109510 |
通讯作者 | Ren, Pan(renp@foxmail.com) |
英文摘要 | NiCrAlYHfSi coating and Ni+CrAlYHfSiN coating were deposited on gamma-TiAl alloy by magnetron sputtering. This work mainly focuses on the influence of cracks on the oxidation resistance of coatings, and the suppression cracking effect by doping nitrides. It was found that longitudinal cracks in the NiCrAlYHfSi coating increase with oxidation time prolonged. Cracks in NiCrAlYHfSi coating provide quick-diffusion channels for Ti and O ions. The Ni+CrAlYHfSiN coating is intact crack free during the whole oxidation process. Owing to the "fix effect" of nitrides, the Ni+CrAlYHfSiN composite coating effectively inhibits Ti diffusing to the surface to destroy the integrity of Al2O3 scale. |
资助项目 | National Nature Science Foundation of China[52001137] ; Fundamental Research Funds for the Central Universities[21617339] ; Science and Technology Program of Guangzhou, Guangzhou, China[202007020008] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000657395600002 |
资助机构 | National Nature Science Foundation of China ; Fundamental Research Funds for the Central Universities ; Science and Technology Program of Guangzhou, Guangzhou, China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/160252] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Ren, Pan |
作者单位 | 1.Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Peoples R China 2.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.Northeastern Univ, Shenyang Natl Lab Mat Sci, Corros & Protect Div, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Yang, Yingfei,Xiao, Qin,Ren, Pan,et al. Improved oxidation resistance of gamma-TiAl intermetallics by sputtered Ni plus CrAlYHfSiN composite coating[J]. CORROSION SCIENCE,2021,187:11. |
APA | Yang, Yingfei,Xiao, Qin,Ren, Pan,Li, Wei,Zhu, Shenglong,&Wang, Fuhui.(2021).Improved oxidation resistance of gamma-TiAl intermetallics by sputtered Ni plus CrAlYHfSiN composite coating.CORROSION SCIENCE,187,11. |
MLA | Yang, Yingfei,et al."Improved oxidation resistance of gamma-TiAl intermetallics by sputtered Ni plus CrAlYHfSiN composite coating".CORROSION SCIENCE 187(2021):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论