INVESTIGATIONS ON THERMAL STABILITY OF FATIGUE DISLOCATION STRUCTURES IN A DOUBLE-SLIP-ORIENTED Cu SINGLE CRYSTAL

CORC > 金属研究所 > 中国科学院金属研究所

	INVESTIGATIONS ON THERMAL STABILITY OF FATIGUE DISLOCATION STRUCTURES IN A DOUBLE-SLIP-ORIENTED Cu SINGLE CRYSTAL
	Guo Weiwei 1; Qi Chengjun 1; Li Xiaowu 1
刊名	ACTA METALLURGICA SINICA
	2013
卷号	49 期号:1 页码:107-114
关键词	CHANNELING CONTRAST TECHNIQUE CYCLIC DEFORMATION-BEHAVIOR POLYCRYSTALLINE COPPER ANNEALING TWINS SEM ORIENTATION AMPLITUDE METALS BANDS Cu single crystal fatigue dislocation structure thermal stability recrystallization annealing twin
ISSN号	0412-1961
其他题名	INVESTIGATIONS ON THERMAL STABILITY OF FATIGUE DISLOCATION STRUCTURES IN A DOUBLE-SLIP-ORIENTED Cu SINGLE CRYSTAL
英文摘要	Although comprehensive research findings of the cyclic deformation and dislocation structures of Cu single crystals with various orientations have been well established over the four decades, studies on the thermal stability of dislocation structures in fatigued Cu single crystals are still rarely reported. In the present work, (2) over bar 33 Cu single crystals oriented for coplanar double slip were firstly cyclically deformed at different plastic strain amplitudes gamma(pl) up to saturation, and then annealed at different temperatures for 30 mm. The dislocation structures induced by cyclic deformation as well as the microstructural changes resulting from subsequent annealing treatments were detected by using the electron channeling contrast (ECC) technique in SEM and TEM. It was found that the dislocation structures have undergone an obvious process of recovery at 300 degrees C, and the recrystallization even partially takes place in the sample fatigued at high gamma(pl). However, at 500 and 800 degrees C, the violent recrystallization takes place in all crystals and a large number of annealing twins have appeared. As the plastic strain amplitude and accumulated plastic strain increase, the degree of strain concentration would be significantly aggravated, providing a higher local strain energy for the occurrence of recrystallization and the initiation of twins, so that the recrystallization takes place more noticeably, and annealing twins become coarser and the number of them increases notably. The formation of annealing twins is closely related to the appearance of stacking faults. The DSC measurements demonstrated that the recrystallization process and the formation process of twins should be a gradually-developing process, instead of a suddenly-forming process.
资助项目	[National Natural Science Foundation of China] ; [Fundamental Research Funds for the Central Universities of China] ; [Specialized Research Fund for the Doctoral Program of Higher Education of China]
语种	英语
CSCD记录号	CSCD:4748768
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/146305]
专题	金属研究所_中国科学院金属研究所
作者单位	1.中国科学院金属研究所 2.上海市地震局
推荐引用方式 GB/T 7714	Guo Weiwei,Qi Chengjun,Li Xiaowu. INVESTIGATIONS ON THERMAL STABILITY OF FATIGUE DISLOCATION STRUCTURES IN A DOUBLE-SLIP-ORIENTED Cu SINGLE CRYSTAL[J]. ACTA METALLURGICA SINICA,2013,49(1):107-114.
APA	Guo Weiwei,Qi Chengjun,&Li Xiaowu.(2013).INVESTIGATIONS ON THERMAL STABILITY OF FATIGUE DISLOCATION STRUCTURES IN A DOUBLE-SLIP-ORIENTED Cu SINGLE CRYSTAL.ACTA METALLURGICA SINICA,49(1),107-114.
MLA	Guo Weiwei,et al."INVESTIGATIONS ON THERMAL STABILITY OF FATIGUE DISLOCATION STRUCTURES IN A DOUBLE-SLIP-ORIENTED Cu SINGLE CRYSTAL".ACTA METALLURGICA SINICA 49.1(2013):107-114.