Oxidation and cracking/spallation resistance of ZrB2-SiC-TaSi2-Si coating on siliconized graphite at 1500 degrees C in air | |
Ren, Yan1,4; Qian, Yuhai4; Xu, Jingjun4; Jiang, Yan2,3; Zuo, Jun4; Li, Meishuan4 | |
刊名 | CERAMICS INTERNATIONAL
![]() |
2020-04-01 | |
卷号 | 46期号:5页码:6254-6261 |
关键词 | Coating Oxidation resistance ZrB2-SiC-TaSi2 Vapor silicon infiltration |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2019.11.095 |
通讯作者 | Qian, Yuhai(yhqian@imr.ac.cn) |
英文摘要 | A ZrB2-SiC-TaSi2-Si coating on siliconized graphite substrate was prepared by a combination process of slurry brushing and vapor silicon infiltration. The high-temperature oxidation behavior and cracking/spallation resistance of the as-prepared coating were investigated in detail. It was revealed that the oxidation kinetics at 1500 degrees C in static air followed a parabolic law with a relatively low oxidation rate constant down to 0.27 mg/(cm(2).h(0.5)). The crack area ratio of the as-prepared coating was determined as 3.8 x 10(-3) after severe thermal cycling from 1500 degrees C to room temperature for 20 times. Apart from the formation of ZrO2 as skeleton phase with SiO2 as infilling species, the good oxidation and cracking/spallation resistance of the coating also could be attributed to its unique duplex-layered structure, i.e., a dense ZrB2-SiC-TaSi2-Si major layer filled with Si and an outermost Si cladding top layer. Meanwhile, the strong adhesion strength of the SiC transition layer with the graphite substrate and the outer ZrB2-SiC-TaSi2-Si layer was a vital factor as well. |
资助项目 | National Natural Science Foundation of China[51571203] ; National Natural Science Foundation of China[51571205] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000515196800091 |
资助机构 | National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/137546] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Qian, Yuhai |
作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Northeastern Univ, Sch Mat Sci & Engn, Inst Ceram & Powder Met, Shenyang 110819, Peoples R China 3.Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Ren, Yan,Qian, Yuhai,Xu, Jingjun,et al. Oxidation and cracking/spallation resistance of ZrB2-SiC-TaSi2-Si coating on siliconized graphite at 1500 degrees C in air[J]. CERAMICS INTERNATIONAL,2020,46(5):6254-6261. |
APA | Ren, Yan,Qian, Yuhai,Xu, Jingjun,Jiang, Yan,Zuo, Jun,&Li, Meishuan.(2020).Oxidation and cracking/spallation resistance of ZrB2-SiC-TaSi2-Si coating on siliconized graphite at 1500 degrees C in air.CERAMICS INTERNATIONAL,46(5),6254-6261. |
MLA | Ren, Yan,et al."Oxidation and cracking/spallation resistance of ZrB2-SiC-TaSi2-Si coating on siliconized graphite at 1500 degrees C in air".CERAMICS INTERNATIONAL 46.5(2020):6254-6261. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论