Corrosion of RE2Si2O7 (RE = Y, Yb, and Lu) environmental barrier coating materials by molten calcium-magnesium-alumino-silicate glass at high temperatures | |
Tian, Zhilin2,3; Ren, Xiaomin1,2; Lei, Yiming1,2; Zheng, Liya2; Geng, Wanrong1,2; Zhang, Jie2; Wang, Jingyan2 | |
刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY |
2019-11-01 | |
卷号 | 39期号:14页码:4245-4254 |
关键词 | Rare earth silicates Corrosion Calcium-magnesium-alumino-silicate Environmental barrier coating materials |
ISSN号 | 0955-2219 |
DOI | 10.1016/j.jeurceramsoc.2019.05.036 |
通讯作者 | Zhang, Jie(jiezhang@imr.ac.cn) ; Wang, Jingyan(jywang@imr.ac.cn) |
英文摘要 | With the increased demand for high operating temperature of gas turbine engines, corrosion by molten calcium-magnesium-alumino-silicate (CMAS) exhibits a significant challenge to the development of durable environmental barrier coatings (EBCs). EBC candidates, gamma-Y2Si2O7, beta-Yb2Si2O7, and beta-Lu2Si2O7 were explored on their corrosion resistance to CMAS melts at 1300 degrees C and 1500 degrees C for 50 h. Interaction and degradation mechanisms were investigated and the corrosion behaviors showed different trends at high temperatures. At 1300 degrees C, RE2Si2O7 dissolves into CMAS melts and apatite phases reprecipitate forming a thick recession layer. However, when the temperature increases to 1500 degrees C, CMAS melts vigorously penetrate through the grain boundary of RE2Si2O7 and 'blister' cracks form throughout the samples. The reduced grain boundary stability at 1500 degrees C promotes the penetration of CMAS melts in RE2Si2O7. Grain boundary engineering is critically demanded to optimize CMAS corrosion at high temperatures. |
资助项目 | National Key R&D Program of China[201711E130703201] ; National Natural Science Foundation of China[51772302] ; CAS International Cooperation Key Program[174321KYSB20180008] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000476965000038 |
资助机构 | National Key R&D Program of China ; National Natural Science Foundation of China ; CAS International Cooperation Key Program |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/134760] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhang, Jie; Wang, Jingyan |
作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China 2.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Tian, Zhilin,Ren, Xiaomin,Lei, Yiming,et al. Corrosion of RE2Si2O7 (RE = Y, Yb, and Lu) environmental barrier coating materials by molten calcium-magnesium-alumino-silicate glass at high temperatures[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2019,39(14):4245-4254. |
APA | Tian, Zhilin.,Ren, Xiaomin.,Lei, Yiming.,Zheng, Liya.,Geng, Wanrong.,...&Wang, Jingyan.(2019).Corrosion of RE2Si2O7 (RE = Y, Yb, and Lu) environmental barrier coating materials by molten calcium-magnesium-alumino-silicate glass at high temperatures.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,39(14),4245-4254. |
MLA | Tian, Zhilin,et al."Corrosion of RE2Si2O7 (RE = Y, Yb, and Lu) environmental barrier coating materials by molten calcium-magnesium-alumino-silicate glass at high temperatures".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 39.14(2019):4245-4254. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论