Effect of Y content on interface reaction and wettability between a nickel-base single crystal superalloy melt and ceramic mould | |
Zi, Yun1,2; Meng, Jie1; Zhang, Chaowei1; Yang, Yanhong1; Zhou, Yizhou1; Ding, Yutian3 | |
刊名 | JOURNAL OF ALLOYS AND COMPOUNDS |
2019-06-15 | |
卷号 | 789页码:472-484 |
关键词 | Nickel-base single crystal superalloy melt Ceramic mould Interface reaction Wettability Y content |
ISSN号 | 0925-8388 |
DOI | 10.1016/j.jallcom.2019.03.037 |
通讯作者 | Meng, Jie(jmeng@imr.ac.cn) ; Zhou, Yizhou(yzzhou@imr.ac.cn) |
英文摘要 | In this paper, the effect of Y content on interface reaction and wettability between a nickel-base single crystal supperalloy melt and ceramic mould were studied by means of sessile drop tests. The microstructural characterization of the alloy-ceramic interface and the elemental compositions of reaction products were performed by scanning electron microscope (SEM) and electron probe micro-analyzer (EPMA), the phases of reaction products were identified by X-ray diffraction (XRD), and the surface analysis of reaction products was carried out by X-ray photoelectron spectroscopy (XPS). The results showed that Al and Hf in the alloy reacted with SiO2 in the ceramic mould when Y content was lower than 0.011 wt%, and the reaction products were Al2O3 and HfO2, with little change in the wetting angle. However, when Y content was higher than 0.017 wt%, Y and Al in the alloy reacted with SiO2 in the ceramic mould, and the wetting angle decreased significantly. 0.017 wt% was the critical concentration of Y content that would cause interface reactions. The reaction products of 0.017 and 0.025 wt% Y alloys were Y3Al2(AlO4)(3), the reaction products of 0.1 wt% Y alloy were Y3Al5O12 and Y4Al2O9, and the reaction products of 0.5 and 1.0 wt% Y alloys were double reaction layer composed of Y2O3 and Y3Al5O12. Si generated by the interface reactions could react with O-2 in the atmosphere to form SiOx during the cooling of the alloy-ceramic couples. (C) 2019 Published by Elsevier B.V. |
资助项目 | National Key R&D Program of China[2017YFA0700704] ; National Natural Science Foundation of China[51601192] ; National Natural Science Foundation of China[5161188] ; National Natural Science Foundation of China[51701210] |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000464542700057 |
资助机构 | National Key R&D Program of China ; National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/132964] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Meng, Jie; Zhou, Yizhou |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Dept Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 3.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Zi, Yun,Meng, Jie,Zhang, Chaowei,et al. Effect of Y content on interface reaction and wettability between a nickel-base single crystal superalloy melt and ceramic mould[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,789:472-484. |
APA | Zi, Yun,Meng, Jie,Zhang, Chaowei,Yang, Yanhong,Zhou, Yizhou,&Ding, Yutian.(2019).Effect of Y content on interface reaction and wettability between a nickel-base single crystal superalloy melt and ceramic mould.JOURNAL OF ALLOYS AND COMPOUNDS,789,472-484. |
MLA | Zi, Yun,et al."Effect of Y content on interface reaction and wettability between a nickel-base single crystal superalloy melt and ceramic mould".JOURNAL OF ALLOYS AND COMPOUNDS 789(2019):472-484. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论