THE INFLUENCE OF LOADING WAVE-FORM ON CORROSION-FATIGUE CRACK-PROPAGATION | |
WANG, ZF; LI, J; WANG, JQ; KE, W | |
刊名 | CORROSION SCIENCE |
1995-10-01 | |
卷号 | 37期号:10页码:1551-1565 |
ISSN号 | 0010-938X |
通讯作者 | WANG, ZF() |
英文摘要 | The influence of loading waveform on crack growth rate (da/dN) of corrosion fatigue (CF) was studied for iron in 3.5%NaCl and 3.5%NaCl + 1%NaNO2 solutions at different applied potentials. The results showed that the effect of loading mode on da/dN of CF depends on the stress intensity factor range, the applied potential and the passivation state of system. The action mechanism of the loading waveform in the different conditions is discussed. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:A1995RW94400003 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/125973] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | WANG, ZF |
作者单位 | CHINESE ACAD SCI,INST CORROS & PROTECT MET,CORROS SCI LAB,SHENYANG 110015,PEOPLES R CHINA |
推荐引用方式 GB/T 7714 | WANG, ZF,LI, J,WANG, JQ,et al. THE INFLUENCE OF LOADING WAVE-FORM ON CORROSION-FATIGUE CRACK-PROPAGATION[J]. CORROSION SCIENCE,1995,37(10):1551-1565. |
APA | WANG, ZF,LI, J,WANG, JQ,&KE, W.(1995).THE INFLUENCE OF LOADING WAVE-FORM ON CORROSION-FATIGUE CRACK-PROPAGATION.CORROSION SCIENCE,37(10),1551-1565. |
MLA | WANG, ZF,et al."THE INFLUENCE OF LOADING WAVE-FORM ON CORROSION-FATIGUE CRACK-PROPAGATION".CORROSION SCIENCE 37.10(1995):1551-1565. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论