PREPARATION OF POWDER METALLURGY Ti-22Al-24Nb-0.5Mo ALLOYS AND ELECTRON BEAM WELDING | |
Wu Jie; Xu Lei; Lu Zhengguan; Cui Yuyou; Yang Rui | |
刊名 | ACTA METALLURGICA SINICA |
2016-09-11 | |
卷号 | 52期号:9页码:1070-1078 |
关键词 | hot isostatic pressing powder metallurgy Ti-22Al-24Nb-0.5Mo alloy porosity electron beam welding |
ISSN号 | 0412-1961 |
DOI | 10.11900/0412.1961.2016.00019 |
通讯作者 | Xu Lei(lxu@imr.ac.cn) |
英文摘要 | Ti2AlNb alloys are considered as a potential structural material for high temperature applications like gas turbine engine components due to their high specific strength and good creep resistance. In this work, pre alloyed powder of Ti-22Al-24Nb-0.5Mo (atomic fraction, %) was prepared by an electrode induction melting gas atomization process and powder metallurgy (PM) alloys was made through a hot isostatic pressing (HIPing) route. PM Ti-22Al-24Nb-0.5Mo rings and plates were welded by electron beam welding (EBW). The microstructure of the welded joints was investigated by OM, SEM, EPMA and X-ray tomography. The effect of post-weld heat treatments (PWHT) on the microhardness, tensile properties and rupture lifetime at 650 degrees C, 360 MPa of the welding joint of PM Ti-22Al-24Nb-0.5Mo plate was also studied. The results show that the HIPing temperature will affect the porosity distribution of PM Ti-22Al-24Nb-0.5Mo alloys. The PM Ti-22Al-24Nb-0.5Mo rings HIPed at 1030 degrees C after 980 degrees C, 2 h, vacuum furnace cooling show good weldability. The fusion zone (FZ), heat affected zone (HAZ) and base metal (BM) of welded joints show homogeneous chemical composition. The microstructures of FZ, HAZ and BM are different while the microhardnesses of FZ, HAZ and BM show no obvious differences. Tensile and stress rupture lifetime testing specimens all fracture in the FZ. It is found that there are a certain number of micro porosity in the FZ of the welded joints. However, the porosity reduces after PWHT, which will improve the high temperature ductility and rupture properties of the PM Ti-22Al-24Nb-0.5Mo welded joints. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000383635700006 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/122675] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xu Lei |
作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wu Jie,Xu Lei,Lu Zhengguan,et al. PREPARATION OF POWDER METALLURGY Ti-22Al-24Nb-0.5Mo ALLOYS AND ELECTRON BEAM WELDING[J]. ACTA METALLURGICA SINICA,2016,52(9):1070-1078. |
APA | Wu Jie,Xu Lei,Lu Zhengguan,Cui Yuyou,&Yang Rui.(2016).PREPARATION OF POWDER METALLURGY Ti-22Al-24Nb-0.5Mo ALLOYS AND ELECTRON BEAM WELDING.ACTA METALLURGICA SINICA,52(9),1070-1078. |
MLA | Wu Jie,et al."PREPARATION OF POWDER METALLURGY Ti-22Al-24Nb-0.5Mo ALLOYS AND ELECTRON BEAM WELDING".ACTA METALLURGICA SINICA 52.9(2016):1070-1078. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论