Surface nanocrystallization of commercial pure titanium induced by SMAT and its properties | |
Zhang, SL; Chen, HN; Lin, QH | |
刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY |
2004-11-01 | |
卷号 | 20期号:6页码:716-718 |
关键词 | surface nanocrystallization pure Ti corrosion |
ISSN号 | 1005-0302 |
通讯作者 | Chen, HN(hnchen@imr.ac.cn) |
英文摘要 | In this paper the preparation technique of surface nanocrystallization in commercial pure titanium was carried out by surface mechanical attrition treatment (SMAT). The mean grain size was calculated by using X-ray diffraction (XRD) and transmission electron microscope (TEM), and the results showed that the mean grain size of the surface was refined to nm level after SMAT treatment. Nanocrystallized surface layers were formed after treated for 5, 15, 30 and 60 min. Microhardness experimental results implied the microhardness obviously increased on the surface layer and it also showed the variation of microhardness at the cross section. Corrosion test results showed the corrosion resistance of the surfaces in the original commercials pure titanium treated by SMAT was not improved in HCl solution. The corrosion micrographs were observed by scanning electron microscope (SEM). |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | JOURNAL MATER SCI TECHNOL |
WOS记录号 | WOS:000225623300022 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/120057] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Chen, HN |
作者单位 | Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, SL,Chen, HN,Lin, QH. Surface nanocrystallization of commercial pure titanium induced by SMAT and its properties[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2004,20(6):716-718. |
APA | Zhang, SL,Chen, HN,&Lin, QH.(2004).Surface nanocrystallization of commercial pure titanium induced by SMAT and its properties.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,20(6),716-718. |
MLA | Zhang, SL,et al."Surface nanocrystallization of commercial pure titanium induced by SMAT and its properties".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 20.6(2004):716-718. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论