Investigation on low cycle fatigue properties of CLAM steel electron beam welded joint at 550 degrees C | |
Cui, Kaixuan1,2; Zhao, Yanyun1; Liang, Mengtian1,2; Huang, Bo1; Huang, Qunying1 | |
刊名 | FUSION ENGINEERING AND DESIGN |
2021-04-01 | |
卷号 | 165 |
关键词 | Low cycle fatigue Electron beam welding CLAM steel Fracture Dislocation |
ISSN号 | 0920-3796 |
DOI | 10.1016/j.fusengdes.2021.112260 |
通讯作者 | Huang, Bo(bo.huang@fds.org.cn) |
英文摘要 | The low cycle fatigue (LCF) properties of structural materials at high temperatures are important for operational safety of fusion reactors. In this work, the investigation on LCF properties of CLAM steel joints welded by electron beam was conducted at strain amplitudes varying from 0.2 % to 0.7 % at 550 degrees C. It is found that the fatigue life and cyclic stress response of welded joints are lower than those of base metal. Continuous cyclic softening is observed in welded joints and base metal during LCF test. A majority of the fatigue cracks initiated at the surface of the the welded joint specimen with several initiation sites and propagated in a transgranular mode. The area of the crack propagation region decreased and the fatigue striation spacing increased with increasing strain amplitude. The cyclic softening is attributed to the coarsening of martensite laths and the reduction in dislocation density. |
资助项目 | National Key Research and Development Plan of China[2018YFE0306100] ; National Key Research and Development Plan of China[2017YFE0300601] ; Provincial Key Research Plan of Anhui[1704a0902021] |
WOS研究方向 | Nuclear Science & Technology |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000632660000001 |
资助机构 | National Key Research and Development Plan of China ; Provincial Key Research Plan of Anhui |
内容类型 | 期刊论文 |
源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/121421] |
专题 | 中国科学院合肥物质科学研究院 |
通讯作者 | Huang, Bo |
作者单位 | 1.Chinese Acad Sci, Inst Nucl Energy Safety Technol, Hefei Inst Phys Sci, Hefei 230031, Anhui, Peoples R China 2.Univ Sci & Technol China, Hefei 230027, Anhui, Peoples R China |
推荐引用方式 GB/T 7714 | Cui, Kaixuan,Zhao, Yanyun,Liang, Mengtian,et al. Investigation on low cycle fatigue properties of CLAM steel electron beam welded joint at 550 degrees C[J]. FUSION ENGINEERING AND DESIGN,2021,165. |
APA | Cui, Kaixuan,Zhao, Yanyun,Liang, Mengtian,Huang, Bo,&Huang, Qunying.(2021).Investigation on low cycle fatigue properties of CLAM steel electron beam welded joint at 550 degrees C.FUSION ENGINEERING AND DESIGN,165. |
MLA | Cui, Kaixuan,et al."Investigation on low cycle fatigue properties of CLAM steel electron beam welded joint at 550 degrees C".FUSION ENGINEERING AND DESIGN 165(2021). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论