Hydrogen embrittlement susceptibility of a Ni-16Mo-7Cr base superalloy | |
Han, FF; He, SX; Liu, M; Zhou, XT | |
刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
![]() |
2018 | |
卷号 | 733期号:-页码:291-298 |
关键词 | STRESS RUPTURE PROPERTIES NICKEL-BASED SUPERALLOY TERM THERMAL EXPOSURE GRAIN-BOUNDARY GH3535 SUPERALLOY INDUCED CRACKING ALLOY TEMPERATURE FRACTURE MICROSTRUCTURE |
ISSN号 | 0921-5093 |
DOI | 10.1016/j.msea.2018.07.077 |
文献子类 | 期刊论文 |
英文摘要 | This study investigated the hydrogen embrittlement sensitivity of a Ni-16Mo-7Cr base superalloy under different hydrogen pre-charging states. Detailed electromicroscopy characterization has been employed on the hydrogen pre-charged alloy after tensile testing to understand the mechanism of hydrogen-assisted cracking. The results show that the tensile strength of the alloy is remarkably decreased with the increasing of hydrogen pre-charging time, whereas the yield strength remains stable all the time. The fractographic study combined with ECCI analysis by Scanning Electron Microscopy demonstrates that the cracks propagated predominantly along the grain boundary in the presence of hydrogen, and a few can propagate along planar dislocation slip bands (DSBs) especially along the intersections between nonparallel DSBs. The proposed hydrogen embrittlement mechanism for the Ni-16Mo-7Cr base superalloy is that the coalescence and widening of the nano-voids, which are resulted from the interaction between the hydrogen and dislocations, cause the crack initiation and propagation along the grain boundary, and further cause the alloy intergranular fracture. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/30976] ![]() |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
作者单位 | Chinese Acad Sci, Thorium Molten Salts Reactor Ctr, Shanghai Inst Appl Phys, Beijing, Peoples R China |
推荐引用方式 GB/T 7714 | Han, FF,He, SX,Liu, M,et al. Hydrogen embrittlement susceptibility of a Ni-16Mo-7Cr base superalloy[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2018,733(-):291-298. |
APA | Han, FF,He, SX,Liu, M,&Zhou, XT.(2018).Hydrogen embrittlement susceptibility of a Ni-16Mo-7Cr base superalloy.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,733(-),291-298. |
MLA | Han, FF,et al."Hydrogen embrittlement susceptibility of a Ni-16Mo-7Cr base superalloy".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 733.-(2018):291-298. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论