Effect of Ni-Re diffusion barrier on Ni-Al coating structure and its oxidation in dry CO2 GAS at 650°C
Li, M. ; Zhou, C. ; Zhang, J. ; Young, D.J.
2017
会议名称 Corrosion and Prevention 2017
关键词 Aluminum alloys
Aluminum coatings
Binary alloys
Carbon dioxide
Cementing (shafts)
Corrosion prevention
Corrosion resistant alloys
Corrosion resistant coatings
Diffusion barriers
Diffusion coatings
Interdiffusion (solids)
Intermetallics
Internal oxidation
Iron alloys
Metallic matrix composites
Nickel coatings
Nickel compounds
Oxidation resistance
Rhenium alloys
Thermodynamic stability
Al-pack cementation
Alloy substrates
CO2 corrosion
Intermetallic phase
Intermetallic precipitates
Ni-al coatings
Nickel aluminide coatings
Oxidation process
Aluminum corrosion
卷号 2017-November
URL标识 查看原文
内容类型 会议论文
URI标识 http://www.corc.org.cn/handle/1471x/5943930
专题 北京航空航天大学
推荐引用方式 GB/T 7714
Li, M.,Zhou, C.,Zhang, J.,et al. Effect of Ni-Re diffusion barrier on Ni-Al coating structure and its oxidation in dry CO2 GAS at 650°C[C]. 见:Corrosion and Prevention 2017.