A Numerical Study of Cracks Appearance on Tungsten Surface After High Intense Pulsed Ion Beam Irradiation | |
Shahid, Ijaz; Shen, Jie; Yu, Xiao; Zhang, Jie; Zhong, Haowen; Cui, Xiaojun; Liang, Guoying; Huang, Wanying; Zhang, Shijian; Yan, Sha | |
刊名 | JOURNAL OF FUSION ENERGY |
2018 | |
卷号 | 37页码:261-269 |
关键词 | Tungsten High intense pulsed ion beam J-integral Finite element method Fracture toughness |
ISSN号 | 0164-0313 |
DOI | 10.1007/s10894-018-0186-x |
URL标识 | 查看原文 |
收录类别 | SCIE |
WOS记录号 | WOS:000444828500006 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/5929984 |
专题 | 北京航空航天大学 |
推荐引用方式 GB/T 7714 | Shahid, Ijaz,Shen, Jie,Yu, Xiao,et al. A Numerical Study of Cracks Appearance on Tungsten Surface After High Intense Pulsed Ion Beam Irradiation[J]. JOURNAL OF FUSION ENERGY,2018,37:261-269. |
APA | Shahid, Ijaz.,Shen, Jie.,Yu, Xiao.,Zhang, Jie.,Zhong, Haowen.,...&Le, Xiaoyun.(2018).A Numerical Study of Cracks Appearance on Tungsten Surface After High Intense Pulsed Ion Beam Irradiation.JOURNAL OF FUSION ENERGY,37,261-269. |
MLA | Shahid, Ijaz,et al."A Numerical Study of Cracks Appearance on Tungsten Surface After High Intense Pulsed Ion Beam Irradiation".JOURNAL OF FUSION ENERGY 37(2018):261-269. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论