Low-pressure arc plasma-assisted nitriding of AISI 304 stainless steel | |
Y. H. Zhao ; B. H. Yu ; L. M. Dong ; H. Du ; J. Q. Xiao | |
刊名 | Surface & Coatings Technology
![]() |
2012 | |
卷号 | 210页码:90-96 |
关键词 | Low-pressure arc plasma-assisted nitriding Austenitic stainless steel Austenite Microhardness austenitic stainless-steel immersion ion-implantation low-temperature glow-discharge tribological properties nitrogen layer spectroscopy behavior |
ISSN号 | 0257-8972 |
中文摘要 | AISI 304 stainless was modified by low-pressure arc plasma-assisted nitriding (PAN) process at different temperatures. The structure, micrographs and composition depth profile were investigated by X-ray diffraction (XRD), optical microscope, scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS), respectively. Microhardness profiles and corrosion behavior in 3.5% NaCl solution were measured by Vicker microhardness tester and potentiodynamic polarization curves, respectively. The results showed that the nitriding temperature had much effect on the phase composition, thickness and microhardness profiles of the nitrided layers. At lower temperature than 430 degrees C, expanded austenite phase was the major phase, while for higher temperature some iron nitride and CrN phases precipitated. The thickness of the nitrided layers increased with the nitriding temperature. The surface nitrogen concentration obtained was in the range of 23 and 27 at.%. The nitriding produced a surface hardening that can reach microhardness value up to 1300 HV0.05 and the hardening effect was analyzed. For lower temperature than 430 degrees C, the corrosion resistance of nitrided samples was not deteriorated. Crown Copyright (C) 2012 Published by Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2013-02-05 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/60492] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Y. H. Zhao,B. H. Yu,L. M. Dong,et al. Low-pressure arc plasma-assisted nitriding of AISI 304 stainless steel[J]. Surface & Coatings Technology,2012,210:90-96. |
APA | Y. H. Zhao,B. H. Yu,L. M. Dong,H. Du,&J. Q. Xiao.(2012).Low-pressure arc plasma-assisted nitriding of AISI 304 stainless steel.Surface & Coatings Technology,210,90-96. |
MLA | Y. H. Zhao,et al."Low-pressure arc plasma-assisted nitriding of AISI 304 stainless steel".Surface & Coatings Technology 210(2012):90-96. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论