Study on Corrosion Behavior of Weld Bead by Tungsten Inert Gas Welding China Low Activation Martensitic Steel in Static Oxygen-Saturated Pb-Bi at 500 degrees C | |
Chen, Gang[1]; Lei, Yucheng[2]; Zhu, Qiang[3]; Li, Tianqing[4]; Wang, Dan[5]; Ju, Na[6]; Xiao, Longren[7]; Luo, Meng[8] | |
刊名 | CORROSION |
2019 | |
卷号 | 75期号:4页码:408-416 |
关键词 | CLAM steel post-weld heat treatment static corrosion weld bead |
ISSN号 | 0010-9312 |
DOI | http://dx.doi.org/10.5006/3066 |
URL标识 | 查看原文 |
收录类别 | SCI(E) ; EI |
WOS记录号 | WOS:000462158900012 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/5323049 |
专题 | 江苏大学 |
作者单位 | 1.[1]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 2.[2]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 3.[3]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 4.[4]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 5.[5]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 6.[6]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 7.[7]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. 8.[8]Jiangsu Univ, Sch Mat Sci & Engn, 301 XueFu Rd, Zhenjiang 212013, Jiangsu, Peoples R China. |
推荐引用方式 GB/T 7714 | Chen, Gang[1],Lei, Yucheng[2],Zhu, Qiang[3],et al. Study on Corrosion Behavior of Weld Bead by Tungsten Inert Gas Welding China Low Activation Martensitic Steel in Static Oxygen-Saturated Pb-Bi at 500 degrees C[J]. CORROSION,2019,75(4):408-416. |
APA | Chen, Gang[1].,Lei, Yucheng[2].,Zhu, Qiang[3].,Li, Tianqing[4].,Wang, Dan[5].,...&Luo, Meng[8].(2019).Study on Corrosion Behavior of Weld Bead by Tungsten Inert Gas Welding China Low Activation Martensitic Steel in Static Oxygen-Saturated Pb-Bi at 500 degrees C.CORROSION,75(4),408-416. |
MLA | Chen, Gang[1],et al."Study on Corrosion Behavior of Weld Bead by Tungsten Inert Gas Welding China Low Activation Martensitic Steel in Static Oxygen-Saturated Pb-Bi at 500 degrees C".CORROSION 75.4(2019):408-416. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论