生物可降解聚酯PBS的合成工艺研究 | |
夏西木卡玛尔·买买提; 王永垒; 吾满江·艾力 | |
刊名 | 生物技术 |
2011 | |
卷号 | 21期号:3页码:74-76 |
关键词 | polyester(1,4-butanediol-succinic acid) biodegradable the titanium catalyst polycondensation |
ISSN号 | 1004-311X |
其他题名 | synthesis of biodegradable pbs polyester |
中文摘要 | 目的:为了提高1,4-丁二醇的附加值和开发新型的生物可降解材料。方法:以钛酸四丁酯为催化剂通过酯化缩聚合成了聚丁二酸丁二醇酯(PBS)。考察了醇酸摩尔比、催化剂用量、反应温度、反应时间等因素对酯化率的影响。结果:醇酸物质的量比为1∶1.2,催化剂用量为0.6%(质量百分含量),反应温度220℃,反应时间6h,酯化率可达98.7%,平均分子量和分子量分布分别为:Mn=182197,Mw/Mn=1.626406。利用红外谱(IR)、凝胶渗透色谱(GPC)对产物进行了表征确认。 |
英文摘要 | Objective:In order to improve the value of 1,4-butanediol and develop new biodegradable material.Method:Synthesis of polyester(1,4-butanediol-succinic acid)by esterificational polycondensation from 1,4-butanediol and succinic acid as raw materials,and using tetrabutyl titanate as the catalyst were studied.Reaction conditions including reaction time,temperature and catalyst amount on the esterification rate were optimized.Result:The mole ratio of hydroxy-acid was 1∶1.2,catalyst amount was 0.6%,reaction temperature was 220℃,reaction time was 6h,esterification rate was 98.7%,average molecular weight and molecular weight distribution were:Mn=182197,Mw/Mn=1.626406.The chemical structure of PBS was characterized by IR and GPC. |
学科主题 | Engineering (provided by Thomson Reuters) |
公开日期 | 2012-11-29 |
内容类型 | 期刊论文 |
源URL | [http://ir.xjipc.cas.cn/handle/365002/1565] |
专题 | 新疆理化技术研究所_新疆维吾尔自治区精细化工工程技术研究中心 |
作者单位 | 中国科学院新疆理化技术研究所;中国科学院研究生院 |
推荐引用方式 GB/T 7714 | 夏西木卡玛尔·买买提,王永垒,吾满江·艾力. 生物可降解聚酯PBS的合成工艺研究[J]. 生物技术,2011,21(3):74-76. |
APA | 夏西木卡玛尔·买买提,王永垒,&吾满江·艾力.(2011).生物可降解聚酯PBS的合成工艺研究.生物技术,21(3),74-76. |
MLA | 夏西木卡玛尔·买买提,et al."生物可降解聚酯PBS的合成工艺研究".生物技术 21.3(2011):74-76. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论