Synthesis and characterization of superhydrophobic functionalized Cu(OH)2 nanotube arrays on copper foil | |
Chen JM(陈建敏) | |
刊名 | Applied Surface Science |
2009 | |
卷号 | 255页码:4015-4019 |
关键词 | Cu(OH)2 nanotube Arrays Superhydrophobic surface Contact angle Wettability |
ISSN号 | 0169-4332 |
通讯作者 | 张平余 |
中文摘要 | Superhydrophobic functionalized cupric hydroxide (Cu(OH)2) nanotube arrays were prepared on copper foils via a facile alkali assistant surface oxidation technique. Thus nanotube arrays of Cu(OH)2 were directly fabricated on the surface of copper foil by immersing in an aqueous solution of NaOH and (NH4)2S2O8. The wettability of the surface was changed from surperhydrophilicity to superhydropho- bicity by chemical modification with 1H,1H,2H,2H-perfluorodecyltriethoxysilane (FAS). The morphol- ogies, microstructures, crystal structure, chemical compositions and states, and hydrophobicity of the films on the copper foil substrates were analyzed by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and water contact angle measurement. It was found that the rough structure of the surface helped to magnify the wettability. The static contact angle (CA) for water is larger than 1608 and the contact angle hysteresis (CAH) is lower than 58 on the modified surface. The high roughness of the nanotube arrays along with the generated C–F chains by chemical modification contributed to the improved superhydrophobicity. The present research is expected to be significant in providing a new strategy for the preparation of novel multifunctional materials with potential industrial applications on copper substrates. |
学科主题 | 材料科学与物理化学 |
收录类别 | SCI |
资助信息 | the National Natural Science Foundation of China (Grant No. 20571024);the Program for Science & Technology Innovation Talents in Universities of Henan Province (Grant No. 2006KYCX001);the Natural Science Foundation of Education Department of Henan Province (Grant No. 2007430013;2008B430020) |
语种 | 英语 |
公开日期 | 2012-11-13 |
内容类型 | 期刊论文 |
源URL | [http://210.77.64.217/handle/362003/2011] |
专题 | 兰州化学物理研究所_固体润滑国家重点实验室 兰州化学物理研究所_先进润滑与防护材料研究发展中心 |
推荐引用方式 GB/T 7714 | Chen JM. Synthesis and characterization of superhydrophobic functionalized Cu(OH)2 nanotube arrays on copper foil[J]. Applied Surface Science,2009,255:4015-4019. |
APA | 陈建敏.(2009).Synthesis and characterization of superhydrophobic functionalized Cu(OH)2 nanotube arrays on copper foil.Applied Surface Science,255,4015-4019. |
MLA | 陈建敏."Synthesis and characterization of superhydrophobic functionalized Cu(OH)2 nanotube arrays on copper foil".Applied Surface Science 255(2009):4015-4019. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论