Photocatalytic H2 evolution over basic zincoxysulfide (ZnS1-x-0.5yOx(OH)(y)) under visible light irradiation | |
Lv GX(吕功煊) | |
刊名 | Applied Catalysis A: General |
2009 | |
卷号 | 363页码:180-187 |
关键词 | Basic zincoxysulfide Solid solution Photocatalyst Visible light Hydrogen evolution |
ISSN号 | 0926-860X |
通讯作者 | 李越湘 |
中文摘要 | A composite visible light photocatalyst was prepared through co-precipitation of Zn(NO3)2 in the mixed solution of aqueous Na2S and NaOH, and calcination in N2 atmosphere. The photocatalyst was characterized by thermogravimetric and differential thermal analysis (TG–DTA), X-ray diffraction (XRD), UV–vis diffusive reflectance spectroscopy (DRS), BET and electrochemistry measurements. Its activity wasevaluated byhydrogen production froman aqueous solution containingNa2SandNa2SO3 as hole scavengers under visible light (l 420 nm) irradiation. The photocatalyst is a mixture of basic zincoxysulfide (ZnS1 x 0.5yOx(OH)y) solid solution and ZnO or only the solid solution. ZnS1 x 0.5yOx(OH)y, which was visible light active, was a solid solution of ZnS with dissolved oxygen and hydroxide groups. Hydroxide groups are very important in the formation and stabilization of the solid solution. The precipitation and calcination temperatures as well as the precursor composition of ZnS1 x 0.5yOx(OH)y have great influence on the photocatalytic activity. With 1:1 calculated molar ratio of ZnS to ZnO (or Zn(OH)2), ZnS1 x 0.5yOx(OH)y photocatalyst prepared via co-precipitation at 373 K and calcination at 673 K underN2 atmosphere exhibits the highest activity. Its apparent quantumyield without noble metal cocatalyst is ca. 3.0% under visible light irradiation. |
学科主题 | 物理化学 |
收录类别 | SCI |
资助信息 | the National Nature Science Foundation of China (No.20763006);National Basic Research Program of China (2009CB220003);Specialized Research Fund for the Doctoral Program of Higher Education of China (20060403006); Program for Changjiang Scholars and Innovative Research Team in University (IRT0730) |
语种 | 英语 |
公开日期 | 2012-09-21 |
内容类型 | 期刊论文 |
源URL | [http://210.77.64.217/handle/362003/553] |
专题 | 兰州化学物理研究所_OSSO国家重点实验室 兰州化学物理研究所_ERC国家工程研究中心 |
推荐引用方式 GB/T 7714 | Lv GX. Photocatalytic H2 evolution over basic zincoxysulfide (ZnS1-x-0.5yOx(OH)(y)) under visible light irradiation[J]. Applied Catalysis A: General,2009,363:180-187. |
APA | 吕功煊.(2009).Photocatalytic H2 evolution over basic zincoxysulfide (ZnS1-x-0.5yOx(OH)(y)) under visible light irradiation.Applied Catalysis A: General,363,180-187. |
MLA | 吕功煊."Photocatalytic H2 evolution over basic zincoxysulfide (ZnS1-x-0.5yOx(OH)(y)) under visible light irradiation".Applied Catalysis A: General 363(2009):180-187. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论