	Temperature dependent mechanical properties of ultra-fine grained FeCo-2V
	A. Duckham ; D. Z. Zhang ; D. Liang ; V. Luzin ; R. C. Cammarata ; R. L. Leheny ; C. L. Chien ; T. P. Weihs
刊名	Acta Materialia
	2003
卷号	51 期号:14 页码:4083-4093
关键词	annealing high temperature tension testing severe plastic deformation ultra-fine grained microstructure yield phenomena alloys deformation ductility strength size
ISSN号	1359-6454
中文摘要	The tensile properties of ultra-fine grained ordered FeCo-2V have been investigated as a function of testing temperature. Samples with grain sizes of 100, 150 and 290 nm have been tested at temperatures ranging from 25 to 500 degreesC. Extremely high yield strengths (up to 2.1 GPa) were measured at room temperature with appreciable ductility of between 3 and 13%. These strengths were found to decline only gradually as the testing temperature was increased to 400 degreesC, while ductility was generally enhanced, up to 22%. The high strengths are attributed to grain boundary strengthening that is particularly effective due to ordering. Measured ductility was dependent on the relative values of yield strength, fracture strength and work hardening rate. Discontinuous yielding and appreciable Luders strain (3-6%) were observed and were dependent on the initial structure and on the testing temperature. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.
原文出处	://WOS:000184761600009
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/35823]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	A. Duckham,D. Z. Zhang,D. Liang,et al. Temperature dependent mechanical properties of ultra-fine grained FeCo-2V[J]. Acta Materialia,2003,51(14):4083-4093.
APA	A. Duckham.,D. Z. Zhang.,D. Liang.,V. Luzin.,R. C. Cammarata.,...&T. P. Weihs.(2003).Temperature dependent mechanical properties of ultra-fine grained FeCo-2V.Acta Materialia,51(14),4083-4093.
MLA	A. Duckham,et al."Temperature dependent mechanical properties of ultra-fine grained FeCo-2V".Acta Materialia 51.14(2003):4083-4093.