Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel

CORC > 金属研究所 > 中国科学院金属研究所

	Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel
	X. Q. Wu ; H. M. Jing ; Y. G. Zheng ; Z. M. Yao ; W. Ke
刊名	Journal of Materials Science
	2004
卷号	39 期号:3 页码:975-985
关键词	refineries
ISSN号	0022-2461
中文摘要	High-temperature naphthenic acid corrosion (NAC) and erosion-corrosion (NAEC) behaviors of pack-aluminized carbon steel have been investigated in laboratory to evaluate the resistance of aluminized layer to the NAC and NAEC. A field erosion-corrosion test of 700 days was also performed in an oil refinery. Parallel tests were carried out for carbon steel. It was found that the aluminized steel exhibited a better NAC resistance only at early testing stage than the carbon steel in high total-acid-number (TAN) environment. The NAC resistance degraded rapidly with increasing testing time, and became even worse than that of the carbon steel at final testing stage, accompanying a step-like or lamellar spallation in the aluminized layer. In low TAN environment, the aluminized steel exhibited a much better resistance to both the NAC and NAEC in comparison with the carbon steel. Similarly a good erosion-corrosion resistance was found for the aluminized steel in actual oil-refining environment although relatively serious erosion-corrosion attack simultaneously took place in the aluminized layer. Based on the above results, possible NAC and NAEC mechanisms for the aluminized steel are discussed. (C) 2004 Kluwer Academic Publishers.
原文出处	://WOS:000188283300028
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/35638]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	X. Q. Wu,H. M. Jing,Y. G. Zheng,et al. Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel[J]. Journal of Materials Science,2004,39(3):975-985.
APA	X. Q. Wu,H. M. Jing,Y. G. Zheng,Z. M. Yao,&W. Ke.(2004).Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel.Journal of Materials Science,39(3),975-985.
MLA	X. Q. Wu,et al."Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel".Journal of Materials Science 39.3(2004):975-985.