Chromizing behaviors of a low carbon steel processed by means of surface mechanical attrition treatment | |
Z. B. Wang ; J. Lu ; K. Lu | |
刊名 | Acta Materialia |
2005 | |
卷号 | 53期号:7页码:2081-2089 |
关键词 | nanostructured low carbon steel surface mechanical attrition treatment high store energy chromizing diffusion nanocrystalline materials aisi 304-stainless-steel iron nitrides diffusion alloys layer nanostructure carbide metals |
ISSN号 | 1359-6454 |
中文摘要 | A nanostructured surface layer of about 20 mu m thick was produced in a low carbon steel plate by means of the surface mechanical attrition treatment (SMAT). Chromizing behaviors of the SMAT sample were investigated by using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Experimental results showed that a much thicker Cr-diffusion layer was obtained in the SMAT sample than in the coarse-grained one after the same chromizing treatment, especially at low temperatures. In the SMAT sample, the formation temperature of chromium compounds was found to be much lower and the amount of chromium carbides was higher than those in the coarse-grained counterpart. The enhanced chromizing kinetics originates from numerous grain boundaries with a high excess stored energy in the nanostructured surface layer due to severe plastic deformation during the SMAT. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/35100] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Z. B. Wang,J. Lu,K. Lu. Chromizing behaviors of a low carbon steel processed by means of surface mechanical attrition treatment[J]. Acta Materialia,2005,53(7):2081-2089. |
APA | Z. B. Wang,J. Lu,&K. Lu.(2005).Chromizing behaviors of a low carbon steel processed by means of surface mechanical attrition treatment.Acta Materialia,53(7),2081-2089. |
MLA | Z. B. Wang,et al."Chromizing behaviors of a low carbon steel processed by means of surface mechanical attrition treatment".Acta Materialia 53.7(2005):2081-2089. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论