In-situ synthesis of Ti3AlC2/TiC-Al2O3 composite from TiO2-Al-C system | |
J. X. Chen ; J. L. Li ; Y. C. Zhou | |
刊名 | Journal of Materials Science & Technology |
2006 | |
卷号 | 22期号:4页码:455-458 |
关键词 | Ti3AlC2 TiC Al2O3 TiO2-Al-C reaction path liquid reaction synthesis mechanical-properties ti3alc2 |
ISSN号 | 1005-0302 |
中文摘要 | Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2:Al:C=3.0:5.0 similar to 5.1:1.8 similar to 2.0. The reaction path for the 3TiO(2)-5Al-2C system was proposed. Al3Ti, Ti2O3, TiO, and delta-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at similar to 900 degrees C of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO(2)-5Al-2C are 13.3 +/- 1.1 GPa, 5.8 +/- 0.3 MPa(.)m(1/2), and 466 +/- 39 MPa, respectively. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/34141] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | J. X. Chen,J. L. Li,Y. C. Zhou. In-situ synthesis of Ti3AlC2/TiC-Al2O3 composite from TiO2-Al-C system[J]. Journal of Materials Science & Technology,2006,22(4):455-458. |
APA | J. X. Chen,J. L. Li,&Y. C. Zhou.(2006).In-situ synthesis of Ti3AlC2/TiC-Al2O3 composite from TiO2-Al-C system.Journal of Materials Science & Technology,22(4),455-458. |
MLA | J. X. Chen,et al."In-situ synthesis of Ti3AlC2/TiC-Al2O3 composite from TiO2-Al-C system".Journal of Materials Science & Technology 22.4(2006):455-458. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论