Short-term oxidation and hot corrosion resistance of a gradient CrN/Cr(1-x)Al(x)N coating | |
M. Zhu ; M. S. Li ; J. J. Xu ; Y. C. Zhou | |
刊名 | Materials and Corrosion-Werkstoffe Und Korrosion |
2010 | |
卷号 | 61期号:11页码:939-946 |
关键词 | high-temperature oxidation aluminide coatings overlay coatings nitride coatings behavior alloy superalloy k38g cr |
ISSN号 | 0947-5117 |
中文摘要 | A CrN/Cr(1-x)Al(x)N coating comprised of an inner layer of CrN and an outer layer of Cr1(1-x)Al(x)N with a gradient distribution of Al was deposited on two different alloys by a reactive sputtering method. Oxidation and hot-corrosion tests of the gradient CrN/Cr1(1-x)Al(x)N coating were performed at different temperatures. The phase compositions and morphologies of the as-deposited coating and the corrosion products were investigated by using XRD and SEM/EDS. The results showed that the gradient CrN/Cr1(1-x)Al(x)N coating exhibited good oxidation resistance at temperatures above 1000 degrees C owing to the formation of an alpha-Al(2)O(3)-rich oxide scale. The coating possessed good hot-corrosion resistance in molten sulfate because the inner CrN layer could supply enough Cr to form a relatively protective Cr(2)O(3) after the Al(2)O(3)-enriched scale failed due to its dissolution in the molten sulfate. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/31789] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | M. Zhu,M. S. Li,J. J. Xu,et al. Short-term oxidation and hot corrosion resistance of a gradient CrN/Cr(1-x)Al(x)N coating[J]. Materials and Corrosion-Werkstoffe Und Korrosion,2010,61(11):939-946. |
APA | M. Zhu,M. S. Li,J. J. Xu,&Y. C. Zhou.(2010).Short-term oxidation and hot corrosion resistance of a gradient CrN/Cr(1-x)Al(x)N coating.Materials and Corrosion-Werkstoffe Und Korrosion,61(11),939-946. |
MLA | M. Zhu,et al."Short-term oxidation and hot corrosion resistance of a gradient CrN/Cr(1-x)Al(x)N coating".Materials and Corrosion-Werkstoffe Und Korrosion 61.11(2010):939-946. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论