Susceptibility of ternary aluminum alloys to cracking during solidification | |
Liu, Jiangwei; Kou, Sindo* | |
刊名 | Acta Materialia |
2017 | |
卷号 | 125页码:513-523 |
关键词 | Welding Ring casting Solidification cracking Hot tearing Al-Mg-Si alloys Al-Cu-Mg alloys Al-Cu-Si alloys Heat transfer Mass transfer |
ISSN号 | 1359-6454 |
DOI | 10.1016/j.actamat.2016.12.028 |
URL标识 | 查看原文 |
WOS记录号 | WOS:000394201500052;EI:20165303196591 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/3334365 |
专题 | 中南大学 |
作者单位 | [Liu, Jiangwei] Cent S Univ, Sch Energy Sci & Engn, Changsha 410083, Hunan, Peoples R China. |
推荐引用方式 GB/T 7714 | Liu, Jiangwei,Kou, Sindo*. Susceptibility of ternary aluminum alloys to cracking during solidification[J]. Acta Materialia,2017,125:513-523. |
APA | Liu, Jiangwei,&Kou, Sindo*.(2017).Susceptibility of ternary aluminum alloys to cracking during solidification.Acta Materialia,125,513-523. |
MLA | Liu, Jiangwei,et al."Susceptibility of ternary aluminum alloys to cracking during solidification".Acta Materialia 125(2017):513-523. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论