Anchoring K+ in Li+ Sites of LiNi0.8Co0.15Al0.05O2 Cathode Material to Suppress its Structural Degradation During High-Voltage Cycling | |
Zhao, Junkai; Wang, Zhixing; Wang, Jiexi; Guo, Huajun; Li, Xinhai; Gui, Weihua; Chen, Ning; Yan, Guochun* | |
刊名 | Energy Technology |
2018 | |
卷号 | 6期号:12页码:2358-2366 |
关键词 | High voltage LiNi0.8Co0.15Al0.05O2 Ni-rich cathode materials Phase transition Structure collapse |
ISSN号 | 2194-4288 |
DOI | 10.1002/ente.201800361 |
URL标识 | 查看原文 |
WOS记录号 | WOS:000455586800007 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/3323810 |
专题 | 中南大学 |
作者单位 | 1.[Zhao, Junkai 2.Guo, Huajun 3.Wang, Zhixing 4.Yan, Guochun 5.Li, Xinhai 6.Wang, Jiexi] Cent S Univ, Sch Met & Environm, Changsha 410083, Hunan, Peoples R China. |
推荐引用方式 GB/T 7714 | Zhao, Junkai,Wang, Zhixing,Wang, Jiexi,et al. Anchoring K+ in Li+ Sites of LiNi0.8Co0.15Al0.05O2 Cathode Material to Suppress its Structural Degradation During High-Voltage Cycling[J]. Energy Technology,2018,6(12):2358-2366. |
APA | Zhao, Junkai.,Wang, Zhixing.,Wang, Jiexi.,Guo, Huajun.,Li, Xinhai.,...&Yan, Guochun*.(2018).Anchoring K+ in Li+ Sites of LiNi0.8Co0.15Al0.05O2 Cathode Material to Suppress its Structural Degradation During High-Voltage Cycling.Energy Technology,6(12),2358-2366. |
MLA | Zhao, Junkai,et al."Anchoring K+ in Li+ Sites of LiNi0.8Co0.15Al0.05O2 Cathode Material to Suppress its Structural Degradation During High-Voltage Cycling".Energy Technology 6.12(2018):2358-2366. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论